Iron-nitrogen-codoped carbon materials derived with core-shell prussian blue polypyrrole as electrocatalyst for effective oxygen reduction reaction

Zhichao Lin,Xinyu Gao,Ying Zhu,Xiuwen Qiao

DOI: https://doi.org/10.13880/j.cnki.65-1174/n.2017.06.002

2017-01-01

Abstract:Due to the slow kinetics of the ORR,noble metal catalysts are generally required on the cathode side,principally platinum and its alloy nanoparticles.However,due to the high cost,the limited natural resources and the poor stability,it is difficult in practical application.Therefore,materials based on nitrogen-doped transition carbon metals have received considerable attention as cheap and effective candidate for ORR.Herein,The Prussian Blue/polypyrrole nanoparticles with core-shell structure were synthesized by in situ polymerization of pyrrole with Prussian blue nanoparticles as templates.Then,iron-nitrogen-codoped carbon nanoparticles (Fe-N-CNPs-X,X represents the pyrolysis temperature) was prepared by high temperature pyrolysis the Prussian Blue/polypyrrole nanoparticles.The particle size of Fe-N-CNPs-X catalyst is about 80 nm.Electrochemical measurements demonstrated that the Fe-N-CNPs-900 exhibits promising catalytic activity towards the ORR in an alkaline medium,-0.17 V potential to produce a significant oxygen reduction current,close to the Pt/C catalyst peak potential (-0.15 V),Moreover,the onset and half-wave (E1/2) potentials of-0.03 and-0.11 V for Fe-N-CNPs-900,very close to Pt/C catalyst(-0.02 V and-0.10 V).The limited current density of Fe-N-CNPs-900 (4.90 mA·cm-2) was comparable to Pt/C (4.86 mA·cm-2).It also shows superior stability compared to the commercial Pt/C catalyst,and good tolerance to methanol cross-over effect.This work opens up a simple way for mass production of Fe-N-CNPs electrocatalysts with high ORR and supercapacitor performance.