Structural Changes Of The Lignin Of Eulaliopsis Binata During Various Pretreatments
Jiebin Tang,Kefu Chen,Jun Xu,Jun Li
2012-01-01
Abstract:Integrated Forest Biorefinery (IFBR) technologies will allow the traditional chemical pulp mills to manufacture high-value chemicals, fuels and/or electric power in addition to pulp. Pretreatment of lignocellulosic materials to extract hemicelluloses combining with subsequently pulping and bleaching can be used for producing dissolving pulp, which naturally fits into the IFBR concept. Three different pretreatments including auto-hydrolysis, organic acid catalyzed hydrolysis and inorganic acid catalyzed hydrolysis, prior to dissolving pulp production from Eulaliopsis binata were studied. Auto-hydrolysis, organic acid and inorganic acid pretreatments were conducted in hot-water without any catalyzer at 170 degrees C for 120min, 2.0% acetic acid solution at 160 degrees C for 60min and 0.5% sulfuric acid solution at 160 degrees C for 30min, respectively.The lignins, isolated from Eulaliopsis binata before and after pretreatment, were characterized by C-13, P-31 Nuclear Magnetic Resonance (NMR) and Fourier transform infrared (FT-IR) spectroscopy. The molecular weight distributions of the ligthns were analyzed by Gas Permeation Chromatography (GPC). NMR analysis confirmed Eulaliopsis binata lignin is of HGS type with a considerable amount of p-coumarate and felurate esters of lignin The major lignin interunit was the beta-O-4 linkage, and a minor amount of phenylcoumarin, resinol, and spirodienone units were also presented. Structural elucidation by NMR also revealed an increase in the degree of condensation of lignin, which is accompanied by a decrease in beta-O-4 linkages that were fragmented and recondensed during the high temperature pretreatments. There were 19%, 38% and 30% decrease of beta-O-4 linkage observed for the auto-hydrolysis, organic acid and inorganic acid pretreatments, respectively. In addition to these changes, the S/G ratio decreased from 0.84 to 0.64, 0.55 and 0.42, respectively. The results from GPC showed that the molecular weight of lignin after pretreatment decreased by 22%, 36% and 12% for the auto-hydrolysis, organic acid and inorganic acid pretreatments, respectively.