Preparation of WO3/TiO2-rGO composites and its photocatalytic performance

Cui-xia LI,Xuan YANG,Gao-wei TAN,Hai-ze JIN,Zhi-zhong YANG

DOI: https://doi.org/10.3969/j.issn.1673-5196.2017.03.006

2017-01-01

Abstract:Taking self-prepared tungsten trioxide(WO3) and graphene oxide(GO) as raw materials, tetrabutyl titanate(TBT) as titanium source, citric acid as hydrolysis inhibitor and surfactant, the WO3/TiO2-GO composite was fabricated with sol-gel process.And then a WO3/TiO2-reductive graphene oxide (WO3/TiO2-rGO) ternary composite was obtained by means of sodium borohydride(NaBH4) reduction.The composite sample was analyzed and characterized with x-ray diffraction(XRD) and transmission electron microscopy(TEM).The effect of GO addition amount and heat-treatment temperature on the structure of the composite and its degradation efficiency of methyl orange was investigated.The result showed that WO3/TiO2 nanoparticles would be uniformly dispersed on the surface of the rGO;the introduction of rGO could effectively inhibit the growth of TiO2 nano-particles, the TiO2 in the composite sample heat-treated at 400, 450 ℃ would be of anatase phase, and with increasing the heat-treatment temperature, the crystal structure would transform from anatase crystal phase into rutile one and, meantime, the crystallite size would grow and the critical line transformation temperature would be about 500 ℃.When the addition amountof GO was 10%, the WO3/TiO2-rGO sample heat-treated at 450 ℃ would have maximal efficiency of photocatalytic degradation of methyl orange, amounting possibly to 95%.