Abstract:Waste waterworks sludge and walnut shell were employed to synthesize a composite catalyst consisting of Fe0/Fe3O4/biochar using a one-step pyrolysis process. The synthesized catalyst was applied to active peroxymonosulfate (PMS) for studying the degradation of methylene blue (MB). Various characterization results confirmed that Fe0 and Fe3O4 were distributed on the surface of composite catalyst, which had a porous structure and large specific surface area of 109.87 m2/g. Owning to these structural properties, the composite catalyst presented desirable catalytic capability and reusability. When 0.4 g/L PMS and 0.3 g/L composite catalyst were added into the MB solution (pH 7), 99.9% MB could be degraded within 60 min at a high reaction rate of 0.1550 min−1, which was much better than that of zero valent iron (ZVI)/PMS system. After the three cycles, the catalyst could still maintain an MB degradation of over 68.0%. The free radical quenching experiments and electron paramagnetic resonance experiments demonstrated that SO 4 − ∙ and HO ∙ were generated during the activation of PMS. The X-ray photoelectron spectrometer analysis revealed that Fe3O4 and various functional groups, such as CO were formed on the composite catalyst, and the Fe2+ was oxidized to Fe3+. Furthermore, the iron leaching experiments indicated that both the homogeneous and heterogeneous reactions occurred during the catalysis of PMS using the synthesized composite catalyst. Acidity and higher temperature were conducive to the catalytic reaction. This study offers a green and sustainable route for simultaneously degrading contaminants and reusing wastes.

Study on Degradation of Methylene Blue Through Heterogeneous Fenton in Slag Catalyst

Fenton-like Degradation of Methylene Blue Using Paper Mill Sludge-Derived Magnetically Separable Heterogeneous Catalyst: Characterization and Mechanism.

Heterogeneous Fenton-like Degradation of Methylene Blue (MB) by Magnetic Nanoparticles Fe3O4@TiO2 in Neutral Condition

Study on the Enhancement of Fenton-like Degradation of Methylene Blue by Foam Glass-Supported Α-Fe2o3/s in a Wide Initial Ph Range

Facile Synthesis of Paper Mill Sludge-Derived Heterogeneous Catalyst for the Fenton-like Degradation of Methylene Blue

Degradation of methylene blue: optimization of operating condition through a statistical technique and environmental estimate of the treated wastewater.

Study on Degradation of Methylene Blue by Tourmaline/H_2O_2 System

Electro-catalytic Degradation of Methylene Blue Wastewater Assisted by Fe2O3-modified Kaolin

Ag2O and NiO Decorated CuFe2O4 with Enhanced Photocatalytic Performance to Improve the Degradation Efficiency of Methylene Blue

Degradation of methylene blue by an E-Fenton process coupled with peroxymonosulfate via free radical and non-radical oxidation pathways

Microwave enhanced Fenton process for the removal of methylene blue from aqueous solution

Degradation of sulfamethazine antibiotics in Fenton‐like system using Fe3O4 magnetic nanoparticles as catalyst

Enhancing the heterogeneous electro-Fenton degradation of methylene blue using sludge-derived biochar-loaded nano zero-valent iron

THE STUDY ON SOME PARAMETERS AFFECTING THE DEGRADATION OF METHYLENE BLUE IN WATER BY ELECTRO-FENTON USING TI/PBO2 ANODE

Effect of Humic Acid on the Degradation of Methylene Blue by Peroxymonosulfate

Synthesis of peroxymonosulfate composite catalyst (Fe0/Fe3O4/biochar) using waterworks sludge and walnut shell for degrading methylene blue

Cu/Fe co-modified nitrogen self-doped biochar as a heterogeneous Fenton-like catalyst for degradation of organic pollutants: Synthesis, performance, and mechanistic study

A Novel Octamolybdate‐based Organic–inorganic Hybrid As Photo‐fenton‐like Catalyst for Degradation of Methylene Blue

Enhanced Fenton catalytic degradation of methylene blue by the synergistic effect of Fe and Ce in chitosan-supported mixed-metal MOFs (Fe/Ce-BDC@CS)

Catalytic degradation of crystal violet and methyl orange in heterogeneous Fenton-like processes

Enhanced Heterogeneous Fenton-Like Degradation by Fe/Cu-TA Encapsulated Melamine Sponge