Abstract:Mn2+ ions doped ZnS semiconductor nanocrystals (ZnS:Mn NCs) were synthesized using colloidal chemical method at 70 degrees C without any capping agents. The as-prepared undoped ZnS and ZnS:Mn NCs were characterized by UV-Vis absorption spectra, fluorescent emission spectra, X-ray powder diffraction (XRD), inductively coupled plasma analysis (ICP), X-ray photoelectron spectroscopy (XPS), Dynamic light scattering (DLS), cyclic voltammogram and electronic transmission microscopy (TEM). The dependence of photoluminescence of ZnS:Mn NCs on dopant concentration was studied. The results show that Mn2+ ions mainly stay at ZnS nanocystal surface, and Mn2+-surface defect state complex was formed, as a result of which, surface defect emission of ZnS nanocrystals was substituted with Mn2+-related PL emission. The strongest fluorescent emission intensity was obtain at 1.85 at% Mn2+ doped ZnS:Mn NCs. The Mn2+ doped ZnS:Mn NCs are of 5 nm in diameter. The emission peak at 575 nm is attributed to d-d (T-4(1) -> (6)A(1)) transition of Mn2+ ions. The existence of Mn2+-related photoluminescence could be well correlated with cyclic voltammogram of Mn2+-doped NCs, where pair of oxidation and reduction peaks were clearly observed due to the doped Mn2+ ions. The adsorbed Mn2+ ions on ZnS NCs produced neither Mn2+ emission nor redox peaks. For heavily doped ZnS:Mn NCs (4.87 at%), redox peaks gap in cyclic voltammogram became larger and new oxidation peak appeared. Correspondingly, when the Mn2+ doping concentration reached 4.87 at%, the Mn2+-related emission totally disappears due to the Mn Mn interactions. This work implys that electrochemical technique is possibly an useful tool to probe the local structure of doped Mn2+ ions.

Influence of Surface Modification on the Optical Properties of ZnS-based Nanomaterials

Surface States and Its Influence on Luminescence in ZnS Nanocrystallite

Surface Sulfurization of ZnO/ZnS Core Shell Nanowires and Shell Layers Dependent Optical Properties

Mechanism of the Enhanced Fluorescence of SiO2-coated ZnS Nanoparticles

Enhanced Mn2+ Emission in Zns:Mn Nanoparticles by Surface Plasmon Resonance of Gold Nanoparticles

Photoluminescence Properties of Cds/Zno Nano-Composites Structure

Enhancement of photoluminescent intensity of ZnS:Mn nanocrystals coated with the polymers

Enhanced Photoluminescence and Characterization of Mn-Doped Zns Nanocrystallites Synthesized in Microemulsion

Luminescent Properties of ZnS∶Mn Nanoparticles Dependent on Doping Concentration

Surface Plasmon Induced Photoluminescence Enhancement in the Au–ZnS Nanocomposite

Photoluminescence enhancement of ZnS:Mn nanoparticles by SiO2 coating

Optimized Doping Concentration of Manganese in Zinc Sulfide Nanoparticles for Yellow-Orange Light Emission

Visible Emission Characteristics from Different Defects of ZnS Nanocrystals

Luminescence enhancement of Mn doped ZnS nanocrystals passivated with zinc hydroxide

Enhanced band edge luminescence of ZnO nanorods after surface passivation with ZnS

Influence of Mn Doping on the Microstructure and Optical Properties of ZnS Nanocrystals

Synthesis And Optoelectrochemical Properties Of Zns:Mn Nanocrystals

Structural and Luminescent Properties of ZnO Nanorods and ZnO/ZnS Nanocomposites

Facile Hydrothermal Synthesis of Mn Doped ZnS Nanocrystals and Luminescence Properties Investigations

Luminescent modulation of zinc sulphide nano-particles by thermal injection method

Influence Factors and Mechanism of Emission of ZnS:Cu Nanocrystals