AnaIysis of SiC Reinforced NickeI-based Wear-resistant Coating Design and Performance

Xian-qun YANG,Li-nan WANG,Yi-ming SUN,Hong-yun ZHAO,Feng-yuan SHU,Fei-yang LV
DOI: https://doi.org/10.3969/j.issn.1672-6634.2016.01.011
2016-01-01
Abstract:Q235 was widely used ,especially applied in the production of mechanical equipment ,but in the requirements of the higher work environment for the surface hardness .Q235 steel often cannot meet the service conditions .By using TIG weld cladding SiC ceramic particles reinforced nickel‐based filler metal composite coating method on the surface of Q 235 to improve the surface hardness and wear resistance .It has been studied the influence of welding current ,welding voltage ,gas flow rate and arc length and speed of welding process parameters on the composite coating quality ;It was analyzed the in‐fluence of SiC ceramic particles with the quality of the nickel‐based filler metal content ratio's to the formability and mechanical properties of composite coating ;On the basis of the test ,the microstructure morphology ,hardness and wear resistance of coating were analyzed ;It was found that coating material cool outward to form dendrites ,isometric in turn near the fusion line in the welding process .It is a good metal ceramic coating brazing material that SiC ceramic particles nickel‐based reinforced metal composite coating made the Q235 carbon steel surface hardness three times greater than that of the parent metal .
What problem does this paper attempt to address?