Abstract:In this work an intercalation-chemistry-based method to synthesize tungstate and tungsten oxide nanosheets was described. A layered bismuth tungstate (Bi2W2O9) was used as the W-containing starting material. After the bismuth oxide layers were leached by a chloride acid, a protonated form, H2W2O7 center dot xH(2)O with sizes of 5-15 mu m, was achieved. The intercalation reaction of n-octylamine with H2W2O7 center dot xH(2)O in heptane and the subsequent dissolution-recrystallization process led to the formation of tungstate-based inorganic organic hybrid nanobelts. Orthorhombic WO3 center dot H2O nanosheets were obtained by removing the organic species of the as WO3 center dot H2O nanosheets at 250-450 degrees C, monoclinic WO3 nanosheets were achieved. The results of XRD, TEM and SEM indicate that the obtained WO3 center dot H2O and WO, were single-crystalline nanosheets with areas of (200-500) nm x (200-500) nor and thicknesses of 10-30 nm. The SAED patterns suggest that the WO3 center dot H2O and WO3 nanosheets possessed a reduced directions of [010] and [001], respectively. N-2 adsorption measurement results indicate that the specific surface areas of the as-obtained WO3 center dot H2O and WO3 nanosheets were up to 250 and 180 m(2)/g, respectively. The formation mechanisms for hybrid nanobelts, WO3 center dot H2O and WO3 nanosheets were discussed. The proposed novel route was efficient in producing two-dimensional WO3 nanosheets on a large scale.

Synthesis and growth mechanism of WO3-ZnO heterostructure

Epitaxial Growth Of Zno Nanowires On Zns Nanobelts By Metal Organic Chemical Vapor Deposition

Synthesis, Characterization and Optical Properties of ZnS Nanobelt/zno Nanoparticle Heterostructures

Structure and Optical Properties of Individual Hierarchical ZnS Nanobelt/zno Nanorod Heterostructures

Metal-Semiconductor Zn-ZnO Core-Shell Nanobelts and Nanotubes

Hierarchical saw-like ZnO nanobelt/ZnS nanowire heterostructures induced by polar surfaces.

Porous ZnO Nanobelts: Synthesis, Mechanism, and Morphological Evolutions

Synthesis, characterization and formation mechanism of single-crystal WO 3 nanosheets via an intercalation-chemistry-based route

Preparation and Characterization of Heterostructure of ZnO@TiO_2 Nanobelts

Structure Analyses and Growth Mechanism of Zno Nanoladders

Polarity-free epitaxial growth of heterostructured ZnO/ZnS core/shell nanobelts

Hydrothermal synthesis of ZnO nanowires and nanobelts on a large scale

Studies on the Synthesis and Growth Mechanism of Single Crystal ZnO Nanowires

Synthesis, Characterization and Formation Mechanism of Single-Crystal Wo3 Nanosheets Via an Intercalation-Chemistry-Based Route

Combined Flame and Solution Synthesis of Nanoscale Tungsten–oxide and Zinc/tin–oxide Heterostructures

ZnS/Zn2SnO4 Biaxial Nanowire Heterostructures

Synthesis of Zno/Cubic (zn, Mg)O Heterostructure Nanorods

Synthesis of Vertically Aligned Ultra-Long ZnO Nanowires on Heterogeneous Substrates with Catalyst at the Root.

Synthesis and photoluminescence properties of comb-like CdS nanobelt/ZnO nanorod heterostructures

TEM investigations on ZnO nanobelts synthesized via a vapor phase growth

Assembly of three-dimensional hetero-epitaxial ZnO/ZnS core/shell nanorod and single crystalline hollow ZnS nanotube arrays.