Development of the Lead-Free Piezoelectric Speakers for Portable Electric Devices

Hui LI,Ning WANG,Bo WANG,Dong-yang HU,Kun-peng FENG,Yang-yang ZHANG

DOI: https://doi.org/10.3969/j.issn.1000-985X.2017.12.034

2017-01-01

Abstract:BaTiO3-doped Bi0.5(Na0.82 K 0.18)0.5TiO3 lead-free thick films were prepared on Pt-electroded alumina substrates using screen printing , their phase structure , microstructure , dielectric , piezoelectric and ferroelectric properties were investigated .The results show that the morphotropic phase boundary (MPB) of (1-x)BNKT-xBaTiO3 thick films was in the x range of 3mol％-7mol％.5mol％ BT-doped BNKT (95BNKT-5BT) thick films exhibited preferable relative dielectric constant of 793, piezoelectric coefficient of 72 pC/N, remnant polarization of 4.35 μC/cm2 , unipolar strain value of 0.817％. However, the addition of 5mol％ BT increases the dielectric loss from 1.1％ to 6.2％, and also increases the coercive field from 35.77 kV/cm to 53.72 kV/cm.In the end, the prepared 95BNKT-5BT thick films were used to make the soud film , with the help of the driver circuit , the lead-free piezoelectric speaker for protable electronic device was developed .