Abstract:The ultrafine dispersing and subsequent self-assembling process of montmorillonite (MMt) micro layers were controlled by pH switch to build sandwich-layer structure of TiO2 intercalated MMt. Different pH controlling processes were carried out during hydrothermal synthesis, and the as-prepared samples were characterized by XRD, SEM, TEM, XPS, FTIR, UV-vis spectra, nitrogen adsorption/desorption analysis, and photocatalytic activities. The FTIR and XRD results reveal that TiO2 is chemically combined with MMt layers by hydrothermal process, which hinders the grain growth and anatase-to-rutile phase transition of loaded TiO2 and the transition temperature is approximately 900 degrees C. The micro-morphology analysis shows that TiO2 nanoparticles could be successfully intercalated into MMt layers by special pH controlling process, resulting in the expansion of interplanar spacing of MMt and increased interface action between TiO2 nanocrystals and MMt sheets. The size of TiO2 intercalated in the MMt is approximately 15 nm, which is much smaller than blank TiO2. Furthermore, comparing with ordinary surface loaded TiO2, the TiO2 nanoparticles sandwiched in MMt layers display much higher UV-light photocatalytic degradation activity and reliable recycling stability to methyl orange (MO), due to more Ti3+ active sites and larger porous volume caused by intercalation. Differed from previous TiO2-MMt, which has directional arrangement and narrowed interlayer spacing of (001) faces of MMt, such novel pH controlling process gives full play to the advantage of clay sheets to build layered limited TiO2, and solves traditional drawbacks of MMt supporting materials such as light barrier and limited mass transfer efficiency in composed photocatalysts. (C) 2018 Published by Elsevier B.V.

An Experimental Study of Synthesis and Application of Al-Ti Pillared Montmorillonite

The photocatalytic activity of the TiO2 pillared montmorillonite after microwave treatment

Stability of organic matters in modified montmorillonites

Enhanced photocatalytic activity of microwave treated TiO2 pillared montmorillonite

A Facile Method of Preparing Sandwich Layered TiO2 in Between Montmorillonite Sheets and Its Enhanced UV-light Photocatalytic Activity

Study on the Adsorption Properties of Al-Pillared Montmorillonites

STUDY ON ADSORPTION OF MODIFIED MONTMORILLONITE FOR METHYLENE BLUE

Adsorption of Direct Green B on Mixed Hydroxy-Fe-al Pillared Montmorillonite with Large Basal Spacing.

Study on the Montmorillonite Organic Intercalated Modification and Intercalated Performance

Preparation and Properties of TiO2/illite Composites Synthesized at Different Hydrothermal Ph Values

Study on Sodium Montmorillonite Modified by Diallylmethyl Alkyl Ammonium Bromide

NOVEL ORGANIC MODIFICATION OF MONTMORILLONITE BY SOLID-STATE REACTION WITH EPOXY COMPOUND

Solvothermal Synthesis and Photocatalytic Activities of Titania Pillared Montmorillonites

TiO2 Intercalated Talc Nanocomposite: Preparation, Characterization, and Its Photocatalytic Performance

A new method for the preparation of modified bentonite used in organic wastewater treatment

Alkali metal-promoted aluminum-pillared montmorillonites: High-performance CO2 adsorbents

Preparation and Properties of Organically Modified Na-Montmorillonite

TiO2/Al-PILC Catalysts Synthesized from a Non-Conventional Aluminum Source of Aluminum and Applied in the Photodegradation of Organic Compounds

[Stability of HDTMA Modified Montmorillonite].

The Sedimentation Capabilities of Hexadecyltrimethylammonium-Modified Montmorillonites

Study on modification of nano-TiO_2 coated on surface of purified diatomite