Abstract:Under various compressive strain rates, sea ice fails in different modes and behaves a brittle-ductile transition. To investigate the mechanism behind the transition, a fieldwork of uniaxial compression tests were performed on the level ice collected from Northeast of the Bohai Sea. The ice owns a typical h2 columnar structure, whose salinity varies from 5.5% to 7.4% while temperature ranges from -15 degrees C to -18.3 degrees C. In the experiments, the samples with uniform dimension of 50 mmx50 mmx107 mm were applied compressive load across to the grain columns. The data shows that the maximum failing stress is 4.7MPa appears at 2.8x10(-3) s(-1) while the lowest value is 1.5 MPa at 4.7x10(-5) s(-1). During the compression tests, the samples failed in three different modes over a wide range of strain rate (4.5x10(-5)-7.5x10(-3) s(-1)). When the failing stress is further categorized by failure mode, the stain rate-stress relation shows a consistent trend in each mode. Under low strain rate, the compressive strength has positive correlation with strain rate. The crack propagation is limited due to the stress concentration at crack tip is relaxed by creep, which leads to a ductile failure. When stain rate is between 9x10(-4) and 5x10(-3) s(-1), the crack was able to develop stably through the specimen along the loading direction and formed a splitting failure. The crack development became unstable and inclined cracks were preferred under high strain rate, where ice failed in a spalling mode. From ductile failure to splitting, the transition is terms of the competition between crack-tip creep and propagation. With sufficient confinement, the spalling dominates the global failure as splitting is suppressed. For both failure mode transitions, the condition is triggered by stain rate. From the measurements, it shows that each failure mode owns an according stress-strain rate relation, which is believed to explain the Brittle-ductile transition. Moreover, the influence of stain rate on the effective elastic modulus is discussed.

Analysis of influence factors on the confined compression strength of sea ice in the Bohai Sea

Experimental Technique for Ice under Dynamic Compressive Loading

Experimental studies on the bohai sea ice shear strength

Experimental studies of the shear strength of sea ice in the Laizhou Bay and around the Yellow River Delta of Bohai Sea

Experimental Study on the Effect of Porosity on the Uniaxial Compressive Strength of Sea Ice in Bohai Sea

Experimental Studies and Characteristics Analysis of Sea Ice Flexurai Strength Around the Bohai Sea

Experimental studies on elastic modulus and flexural strength of sea ice in the bohai sea

Characteristics of sea ice compressive strength in Liaohe Estuary

EXPERIMENTAL STUDY ON SEA ICE TENSILE STRENGTH BASED ON BRAZILIAN TESTS

Techniques for Measuring Ice Physical Parameters and Uniaxial Compressive Strength in the Bohai Coastal and Ship-Base Investigations

Influence of the Loading Direction on the Uniaxial Compressive Strength of Sea Ice Based on Field Measurements

Experimental Study on Flexural Strength and Effective Elastic Modulus of Granular Ice in the Bohai Sea, China

Statistical ice conditions of Bohai Sea

Experiments on Sea Ice Fracture Toughness in the Bohai Sea

The Study On Brittle-Ductile Transition Mechanism And Failure Mode Of Sea Ice Under Uniaxial Compression

Research on Short-term Ice Cases for Predicting Ice Force on Conical Structure in the Bohai Gulf

Preliminary Study of Mechanical Properties of Bohai Ice under Dynamic Loading

Experimental Investigation of Ice Loads on Structures during Quasi-Static Compression Tests

Zones of Bohai for Ice Engineering Projects Based on Physical and Mechanical Parameters of Ice

Method for Testing Shear and Tensile Strengths of Freshwater/Seawater Ice

Investigations on Flexural Strength of a Columnar Saline Model Ice under Circular Plate Central Loading