Synthesis of Thioether Compounds and Their Application in Initiating/Controlling the Radical Polymerization of Styrene
Hao-yu Yu,Jian-wei Shao,Dong Chen,Shi-chao Wang,Li Wang,Wan-tai Yang
DOI: https://doi.org/10.11777/j.issn1000-3304.2018.18107
2018-01-01
Acta Polymerica Sinica
Abstract:With inspiration from the structure of macromolecular thioether generated in the 9H-xanthene-9-thione mediated radical polymerization, five thioethers containing 9-alkyl-9-phenylthio/methylthio-xanthene structure were synthesized. Xanthydrol was selected as the precursor for two 9-substituted xanthene intermediates. 9-(Phenylthio)-9H-xanthene was obtained via a condensation reaction between xanthydrol and thiophenol in the presence of perchloric acid as catalyst. 9-(Methylthio)-9H-xanthene was obtained via the thioetherification of the chlorinated product of xanthydrol with sodium methyl mercaptide. The sulfurated intermediates were deprotonated by n-butyl lithium, and transformed into five target products via substitution reactions with three alkyl halides individually. H-1-NMR, C-13-NMR, FTIR and UV-Vis analyses were conducted to confirm and characterize the thioethers. Afterwards, a systematic study on the polymerization behavior of styrene (St) initiated by the thioethers was carried out in the absence and presence of a thermal initiator. Bulk polymerizations of St were initiated successfully by the thioethers at 80 degrees C with relatively low monomer conversions, and the reactions exhibited uncontrolled polymerization behaviors without obvious increase in number-average molecular weight (M-n) in the polymerization process with the PDI of polymeric products above 3.0. However, when the thioethers were used together with 2,2'-azobis(2,4-dimethyl) valeronitrile (ABVN) in the solution polymerization of St in toluene at 65 degrees C, higher monomer conversions compared with those of bulk polymerization and certain controllability could be achieved, reflected by a linear increase in M-n with conversion. Besides, the effects of molar ratio of ABVN to thioether and reaction temperature on the polymerization behavior of St were investigated in detail. A reduction in the molar ratio of ABVN to thioether would cause a reduction in the concentration of propagating radicals, and lead to a decrease in monomer conversion. But the PDI of polymeric product narrowed down indicating a controllable polymerization. Furthermore, elevated reaction temperature brought about an increased concentration of chain radical, and resulted in a relatively low M-n with a broadened PDI.