Repair of articular cartilage and subchondral defects with a new type biological composite material polyvinyl alcohol/nano-hydroxyapatite and polyamide 66
Tao Guo,Tian-fu Yang,Jie Xiao,Hao Long,Yi-xin Chen,Fu-xing Pei,Yu-bao Li
DOI: https://doi.org/10.3321/j.issn:1673-8225.2008.14.007
2008-01-01
Abstract:Background: Polyvinyl alcohol (PVA) hydrogel has been generally considered as a good substitute material of articular cartilage, nano-hydroxyapatite (n-HA) is widely used to repair bone defect, and polyamide 66 (PA66) polymer has achieved an extensive application in the fields of engineering and medicine owing to its high intensity, strong tenacity and good stability. Objective: Based on physico-chemical characteristics of articular cartilage, this study is designed to prepare a new type of biomaterial composite PVA/n-HA+PA66 and observe the repair of articular cartilage and subchondral defects in rabbit knee joints with PVA/n-HA+PA66. Design time and setting: The animal controlled experiment was performed according to random grouping in Tissue Engineering Laboratory, Department Orthopedics, West China Hospital, Sichuan University from July 2006 to July 2007. Materials: Seventy-two healthy adult New Zealand rabbits were used for the models of articular cartilage and subchondral defects by perforating (5 mm × 5 mm × 5 mm) on the femoral bone joint. PVA/n-HA+PA66 was offered by the Analytical and Testing Center of Sichuan University, its specification was cylinder, diameter 5 mm, height 5 mm; upper layer (PVA) height 1.5 mm, ivory, smooth and tenacious; lower layer (n-HA+PA66) height 3.5 mm, rough and stiff. PVA was porous network, with pore diameter 5-40 μ m, porosity 75.3% and water ratio 71.6%; n-HA+PA66 was also porous, with pore diameter 100-400 μ m and porosity 61.7%. Methods: Seventy-two rabbit models were at random divided into 3 groups (n=24): PVA/n-HA+PA66 implant group, PVA implant group, and control group. Materials were implanted into articular cartilage and subchondral defects in rabbits, while no treatment was given in the control group. Main outcome measures: The macroscopic and histological evaluations of rabbit knee joints were performed at 4, 8, 12 and 24 weeks postoperatively. II collagen was measured by immunohistochemical dyeing. The interfaces of biomaterial implants with articular cartilage and subchondral bone were observed by scanning electron microscope. Results: All 72 rabbits were involved in the result analysis. 1 No infection was observed in all animals with good motion of joints. 2 At 24 weeks postoperatively, the lower layer materials of PVA/n-HA+PA66 got well with surrounding cartilage, which did not degenerate obviously; In PVA implant group, the gap was enlarged between PVA and partly of surrounding cartilage, which did degenerate; Most of the defects had been calcified in the control group. 3 At 24 weeks postoperatively, II collagen immunohistochemical dyeing were positive in gaps between PVA and surrounding cartilage, and in PVA surface; In PVA implant group, positive dyeing was a little increased in gaps between PVA and surrounding cartilage, but weakened in PVA surface and surrounding cartilage; Reduced dyeing was observed in both the defect surface and surrounding cartilage in the control group. 4 At 24 weeks postoperatively, lower layer materials of PVA/n-HA+PA66 were full of bone tissues under scanning electron microscope, and were closely connected with upper layer material PVA; In PVA implant group, bone tissue around the materials receded, and the gap became bigger; The interior defects in the control group were filled with bone tissues, while superior defects with fibrous scar-like tissues that arranged in disorder. Conclusion: The diphase biological composite materials PVA/n-HA+PA66 have good function for replacing articular cartilage and subchondral, with good biocompatibility.