In vitro biocompatibility of mesoporous nano hydroxyapatite/poly lactic acid composite scaffolds with osteoblast in bone tissue engineering

Xinle LUO,Shu HUANG,Jinqi SONG,Weimin ZHU,Kan OUYANG

DOI: https://doi.org/10.3969/j.issn.2095-9958.2017.04-14

2017-01-01

Abstract:Background:At present,the biocompatibility and biomechanical properties of scaffold materials are not satisfactory in bone tissue engineering,and the subsequent degradation of materials is also a problem to be solved.The combination of new materials,methods,techniques and medical research could improve the shape and structure,biocompatibility and degradation rate of scaffolds in bone tissue engineering.Objective:To develop a compound of two materials with better biocompatibility in bone tissue engineering through the construction of scaffolds by mesoporous nano hydroxyapatite/poly lactic acid (nHA/PLLA) composite and the compatibility study of it with osteoblast.Methods:nHA/PLLA composite was prepared by freezing rapid prototyping method;porosity was determined by BET;internal structure was observed by SEM to show physical properties;physical characteristics were presented through X-ray diffraction.The growth,adhesion and proliferation of osteoblasts in nHA/PLLA in vitro were shown by SEM;the amount of osteoblasts in nHA/PLLA were observed and calculated by inverted fluorescence microscope;the influence of nHA/PLLA composite on osteoblasts activity was determined by MTT.Results:nHA/PLLA composite was prepared with the pore size of (164±52) μm and the porosity of 89.3％±1.4％;the modulus of compression of dry and wet nHA/PLLA composite scaffolds were (1354.6±53.7) kPa and (1012.8±61.3) kPa,respectively;MTT results showed that nHA/PLLA composite had no significant influence on osteoblasts activity and with the prolongation of incubation,the amount of osteoblasts adhering to the composite surface and in the mesoporous increased gradually.Conclusions:The nHA/PLLA composite is a kind of scaffold material with high performance in bone tissue engineering,and its advantages include easy preparation,shape and internal structure meeting the requirements of tissue engineering scaffold and good biocompatibility with osteoblasts.