Reconstructing goat mandible defects with inorganic active element bone grafts
M.C. Ye,L. Chou,L.P. Wang,R.X. Li,M. Chen,R. Kang,Y. Zhou,B. Bai,F.F. Gong,J. Huang
DOI: https://doi.org/10.1016/j.ijom.2009.03.411
2009-01-01
Abstract:AIM: To discuss the efficacy and biocompatibility of inorganic active element bone tissue engineering grafts in repairing big box defects in goat's mandible angle. METHODS: The experiment was carried out in the Experimental Center and Related Laboratory, Anhui Provincial Hospital Affiliated to Anhui Medical University from February to December in 2004.①Inorganic active element bone tissue engineering grafts were provided by the Department of Molecular Biocompatibility in Boston University; 21 female healthy goats were offered from the Experimental Animal Center in Anhui Medical University. All the managements were in accordance with the ethical standard of animals.②Fifteen goats were operated on both sides of mandible angle to prepare the big box defects of 30 mm×25 mm×10 mm, with inorganic active element bone tissue engineering grafts put into the left side (graft side) and blank control into the right side (control side) using the matched-pairs design. Fifteen goats with defects were divided into three groups according to the three time points of 4, 8, 12 weeks. While other 6 goats were served as control group, without the operation.③At 4, 8, 12 weeks postoperatively, the goats were examined by X-ray, histological detection and radionuclide imaging to observe the new bone formation in defect area; bone density was measured; the biocompatibility of materials was evaluated by hematological test and marrow stroma cell culture. RESULTS: ①General observation: No goats died on operation, and the wound healed well at Ⅰ period.②X-ray: Bone density increased gradually and the X-ray shadow expanded in graft side, while control side presented lucent shadow.③Radionuclide imaging: In graft side, there were obvious uptakes of the 99mTc-MDP and revascularization; In control side, there was no process of bone regeneration and bone metabolism.④Bone density in graft side increased by degrees, while that in control side maintained at low level, showing no auto-osteogenic phenomenon.⑤Histological detection: Bone defects of graft side had the process of progressing osteogenesis along with the time, calcification and bone marrow formation occurred at 12 weeks. No bone formation was found in control side.⑥Biocompatibility: The blood routine, cell morphology, biochemistry and related enzymological index were all normal in each sample. CONCLUSION: Inorganic active element bone tissue engineering grafts have good function on auto-osteogenesis and revascularization, as well as good biocompatibility. So these grafts will be the main materials in clinic of repairing bone tissue engineering defects.