Preparation and Quality Evaluation of BMP-2 Loaded PPLA Microspheres

Zhen WANG,Gui-mei LIN

DOI: https://doi.org/10.19526/j.cnki.1005-8915.20170104

2017-01-01

Abstract:Bone morphogenetic protein-2 (BMP-2) has been reported to stimulate their osteogenic differentiation both in vitro and in vivo.The purpose of this study was to prepare two-block copolymer polylactic acid-polyethylene glycol (PPLA) microspheres loaded with bone morphogenetic protein (BMP-2) and to study their characterization.The BMP-2/PPLA microspheres were prepared using the water-in-oil-in-water (W/O/W) solvent evaporation method.This work was conducted to optimize the entrapping conditions of the rhBMP-2 loaded PPLA copolymer.The effects on encapsulation efficiency (EE) of the polyvinyl alcohol (PVA) concentration,the PPLA concentration,the ratio of internal water phase to oil phase,the ratio of oil phase to external water phase,stirring time and stirring speed were tested.On the basis of single-factor experiments,the optimum parameters were achieved using orthogonal test.Its morphology was investigated with super depth of field microscope.The partical size and Zeta potential were conducted by means of dynamic light scattering.Encapsulation efficiency was measured by Ultraviolet spectrophotometry (UV).The results showed that the highest EE of BMP-2 was achieved with a PVA concentration of 4％,a PPLA concentrartion of 90 mg/mL,the ratio of internal water phase to oil phase is 1 to 5,the ratio of oil phase to external water phase is 1 to 10 and a stirring time of 1.5 min at 15 000 r/min.Under these optimal conditions,the EE achieved was (79.80 ± 0.06) ％.The super depth of field microscope showed that the microspheres were of spheric morphology and the particle size was homogeneous.Mean diameter and Zeta potential of microspheres were (3.48 ± 0.51) μm and-(23.27 ± 0.76) mV respectively.The microspheres prepared according to the optimal technique parameters assumed good appearance,with a high encapsulation efficiency and good reproducibility.The established preparation technique for BMP-2-1oaded PPLA microspheres is feasible.