Processing optimization for improving freeze-thaw stability of soybean protein isolate by ultrasonic assisted glycosylation
Wang Xibo,Zhang Zeyu,Ge Hongru,Xu Yeye,Xia Ruxin,Jiang Lianzhou
DOI: https://doi.org/10.11975/j.issn.1002-6819.2016.14.036
2016-01-01
Abstract:Soybean protein isolate (SPI) has been widely used in food industry because of its ability to improve texture which is contributing to the nutritional and health benefits of protein-based foods. It can be used as emulsifiers in food emulsions due to the surface-active properties of their constitutive proteins, the storage globulins 7S and 11S. Oil-in-water (o/w) emulsions are thermodynamically unstable systems and sensitive to environmental changes, for example cooling and freezing. Freezing and frozen-food storage can maintain microbiological and chemical stability, while extending the shelf life of food products. There are many potential applications for o/w emulsions that can be frozen and then thawed prior to use, such as refrigerated and frozen food. Nevertheless, most of o/w emulsions are highly unstable when they are frozen and will have rapid breakdown after thawing. When an o/w emulsion is stored at low temperature, a variety of physicochemical processes can occur including ice formation, fat crystallization, freeze-concentration, interfacial phase transitions and biopolymer conformational changes. These phase transitions may lead to creaming, oiling off, coalescence and flocculation of the emulsions, which limit its utilization in frozen food. In order to improve the freeze-thaw stability of SPI, the SPI-D (dextran) grafts were prepared by ultrasonic-assisted glycosylation. Based on the early study of single-factor experiment, we found that the emulsion stability index (ESI) before freeze-thaw and the creaming index (CI) after freeze-thaw had high correlation. So the ESI and CI were set as the response values, the concentration of SPI, ultrasonic temperature and ultrasonic power were as factors, the Box-Behnken model of optimizaiton process was established to improve the emulsifying properties and freeze-thaw stability of SPI. The results showed that under the condition of the concentration of 40 mg/mL SPI, 80 ℃ ultrasonic temperature, 5 W/mL power density, the freeze-thaw stability of glycosylation products attained the optimal level. Compared with the control SPI, the CI of the emulsions prepared by ultrasonic SPI-D grafts decreased by 57.76%, 75.33% and 75.33% respectively after freeze-thaw cycles of 1, 2 and 3 times, the ESI increased by 43.80%, and the particle size of the emulsions maintained at the range of 50-55μm. Comparative study of freeze-thaw stability of emulsions prepared by the mixture of SPI and D, the wet heating SPI-D grafts, the ultrasonic SPI-D grafts and the native SPI was also performed. The results indicated that the CI and ESI of SPI and D mixture had no significant difference compared with the native SPI. The addition of dextran with heating had a little effect on the freeze-thaw stability of SPI, but far more than that of ultrasonic SPI-D grafts. Infrared spectrum analysis showed that the grafts in 3 500-2 990 cm-1 had the wide stretching vibration, the absorption peak migrated from 3 280 to 3 270 cm-1, and the free hydroxyl had the vibration absorption. SPI had the absorption peak in 1 060 cm-1, which migrated to 1 010 cm-1 for the grafts, and the grafts’ absorption of vibration was better than SPI, the carbon-nitrogen (C-N) covalent bond vibration was strengthened, the degree of graft attained 32.43%, indicting that SPI and dextran were based on a combination of covalent bond. From the fluorescent spectra we could see that the maximum absorption wavelength of SPI was red-shifted from 344 to 345 nm, the fluorescence intensity increased to 1 014; scanning electron microscopy showed that the particle state of glycosylation protein became more loose, the intermolecular aggregation degree decreased significantly, and thus the freeze-thaw stability improved significantly. The result provides us a new method for the preparation of SPI with high freeze-thaw stability, which is to modify SPI through ultrasonic-assisted glycosylation. This method provides a theoretical and technical guidance for the industrialization production of SPI which is more suitable for frozen foods.