A Comparative Study on the Morphology and Basic Density of Raw Fiber in Mulberry, Eucommia and Recycled Materials

Zheng GUO,Yu-xiu LI,Ya-fang LEI
DOI: https://doi.org/10.3969/j.issn.1001-7461.2017.05.34
2017-01-01
Abstract:The fiber morphology and basic density of the three kinds of branch woods of Morus alba,Eucommia ulmoides and Tamarix ramosissima were analyzed and compared with the common materials of recombinant wood,and the feasibility of using these three kinds of branch woods reconstituted material was discussed.The results indicated that the fiber length of Morus alba,E.ulmoides,and T.ramosissima were mainly in the ranges of 600-900 μm,700-1 000 μm and 500-800μm,respectively,accounting for 71.33%,79%,and 87% of the total.Width ratio was greater than 33,belonging to the slender fiber type.The average fiber contents of the three were 66.23%,65.01% and 66.82%,respectively,and the cavity ratio was less than 1.The average basic densities of the three were 0.46 g · cm-3,0.49 g · cm-3 and 0.72 g · cm 3,respectively.The average fiber length and the average fiber aspect ratio of E.ulmoides decreased gradually from the bottom to the top of the branch.The average fiber width and wall ratio were low at both ends,high in the middle,and the average fiber content was high at two ends,low in the middle.The mean fiber length,mean fiber length-width ratio and average fiber content of M.alba increased gradually from the bottom to the top.In terms of fiber morphology and basic density,all the three kinds of wood could be used as the quality material for the production of recombinant materials,and eucommia bar better.
What problem does this paper attempt to address?