Effect of shot-peening pre-treatment on TIG-welding braze aluminum alloy to steel

Qi AN,Xinjian YUAN,Wenlong ZHANG,Ruojin ZANG

DOI: https://doi.org/10.11951/j.issn.1005-0299.20150614

IF: 1.8

2015-01-01

Materials Science and Technology

Abstract:To firmly bond aluminum with steel, TIG-welding braze of Zn-coated steel to 5052 aluminum alloy was carried out using Al-Si( 6%~8% ) filler. A shot-peening pre-treatment of the 5052 aluminum plate was performed to investigate its effect on the interfacial microstructure and mechanical properties of the resultant joint. It was found that the grains of fusion welding columnar crystal at the joint are uniformly distributed with the help of shot-peeing to promote the reaction between steel and welded metal. At the same time, the thickness of diffusion layer increased form 6. 0 μm to 9. 5 μm with shot-peening pre-treatment. Further, the mechanical properties of the surface peening significantly improved quality of jiont to achieve a joint tensile-shear strength of 238.6 N/mm.