Effect of Ti-48Al-8Cr-2Ag Coating on the Cast TiAlNb Alloy in the Presence of NaCl and Water Vapor

XI Yanjun,WANG Fuhui
DOI: https://doi.org/10.3321/j.issn:1005-3093.2006.01.009
2006-01-01
Abstract:Ti-48Al-8Cr-2Ag (atomic fraction, %) coating on the cast TiAlNb alloy was produced by magnetron-sputter deposition. The effect of Ti-48Al-8Cr-2Ag nanocrystalline coating on corrosion behavior of cast TiAlNb alloy has been investigated in the presence of NaCl and water vapor at 500-700℃. The results show that corrosion is severely speeded up when the atmosphere contains NaCl and water vapor. With the increase of the temperature, corrosion speed increases. The dense TiO2 scale forms on the surface of the TiAlNb alloy in the presence of NaCl and water vapor at 700℃ due to the effect of the Nb element. The TiAlNb alloy exhibits higher corrosion rate than the alloy with TiAICrAg coating because chloride intruded into α2 phase of the TiAlNb alloy. In addition, higher Cr content in Laves phase is one of the reasons of the lower corrosion rate of the coating.
What problem does this paper attempt to address?