Preparation and performance of crosslinked poly(arylene ether)s-based anion exchange membranes

Xiuqin WANG,Chenxiao LIN,Aimei ZHU,Qiugen ZHANG,Qinglin LIU

DOI: https://doi.org/10.16159/j.cnki.issn1007-8924.2018.02.001

2018-01-01

Abstract:Fuel cells are regarded as one of the most perspective energy conversion devices due to its high efficiency and low pollution.As a critical component of fuel cells,anion exchange membranes (AEMs)still meet the dilemma of low conductivity and high swelling ratio.Herein,crosslinked poly(arylene ether)s-based anion exchange membranes (AEMs) were prepared via olefin metathesis using Grubbs Ⅱ catalyst and crosslinking under thermal treatment.The as-prepared AEMs exhibit obvious microphase separated morphology since the hydrophilic side chain is immiscible with hydrophobic poly (arylene ether)s backbone.Finally,the crosslinked AEMs demonstrate a highest conductivity of 81.1 mS/cm at 80 ℃.The crosslinked structure is effective at enhancing the dimensional stability of the membranes.C-FPAE-PH-1.5 shows a low swelling ratio of 7.51％ at 30 ℃.Furthermore,the crosslinked AEMs show robust alkaline stability.C-FPAE-PH-1.5 remained 93.1％ of its original conductivity after immersing into a 1 mol/L KOH aqueous solution at 60 ℃ for 360 h.