Luminescent properties and synthesis of CaMoO4∶Eu3+ red phosphor by NH4Cl flux

Desheng ZHU,Feng JIANG
DOI: https://doi.org/10.3969/j.issn.1001-9731.2017.03.044
2017-01-01
Abstract:The CaMoO4∶Eu3+ phosphors were synthesized by the high-temperature solid-state reaction method with NH4Cl flux.The optimum synthesis temperature of the powders was studied by using a thermal analyzer (TG-DSC).The internal structures and the surface topographies were tested by X-ray powder diffraction (XRD), scanning electron microscope (SEM), Fourier transform infrared spectrometer (FT-IR) and laser Raman spectroscopy.The luminescence of the crystal was detected by fluorescence spectrometer.The results show that the synthesis temperature of the crystal is 800 ℃.The powders are pure CaMoO4 crystal and have the stable structure.The particles are spherical clusters and the size is about 5/7 μm.The excitation spectrum is mainly composed by a charge transfer band from 200 to 350 nm of O2-→Eu3+ and O2-→Mo6+ and two peaks at 395 nm of 7F0→5L6 and 465 nm of 7F0→5D2.The emission spectrum is composed of a series of peaks from 580 to 750 nm.The main peak is at 615 nm due to the 5D0→7F2 transition of Eu3+.The luminescence of phosphors is the best when the relative of the flux is 4mol%.The best content of Eu3+ is 0.06.
What problem does this paper attempt to address?