UV polymerization and characterization of self-crosslinking polyacrylic acid superabsorbent

an Mamatj,an Amatj,Nurulla Ismayil,Qingdong SHI,Wanting XU

DOI: https://doi.org/10.3969/j.issn.1001-9731.2016.04.037

2016-01-01

Abstract:A self-crosslinking polyacrylic acid superabsorbent was prepared with acrylic acid as raw materials by UV polymerization.The samples were further characterized by means of FT-IR,1 H NMR and SEM.The effects of preparation conditions such as power of ultraviolet light source,irradiation distance and the polymeri-zation temperature on the absorbency were evaluated.The results show that:power the UV lamp was 1 000 W, the polymerization temperature was 1 5 ℃,the light irradiation time was 40 min,and irradiation distance is 1 5 cm.Results show that absorbencies of the resin which is polymerized under the optimum condition are as fol-lows:the deionized water absorbency was 4 391 g/g,the saline water (m(NaCl)=0.9%)absorbency was 206 g/g.Meanwhile,absorbency under load of the resin was compared with other different absorbing resins.