Abstract:For the first time, well-dispersed submicrometer-sized YVO4:Eu3+ hollow spheres were successfully synthesized though a surfactant-free method by employing Y(OH)CO3:Eu3+ colloidal spheres as a sacrificial template and NH4VO3 as a vanadium source. The synthetic process mainly consists of two steps, i.e., hydrothermal reaction and acid erosion. By simply changing the amount of NH4VO3 added, the textural parameters of the as-obtained hollow spheres, such as the inner diameter and shell-thickness, can be easily tuned. Moreover, double-shelled hollow spheres could also be obtained when the amount of NH4VO3 was increased to a certain extent. Particularly, the amorphous colloidal spheres of the template could be completely consumed when the amount of NH4VO3 was in large excess, giving rise to the direct formation of uniform hollow spheres without acid erosion. The possible formation process is discussed in detail. Under ultraviolet excitation, the obtained hollow YVO4: Eu3+ phosphors showed strong red emissions, and the Commission Internationale d'Eclairage (CIE) coordinates of the YVO4:Eu3+ phosphors were closely related with the textural parameters such as the inner diameter, shell-thickness and number of shells, indicating a size-dependent characteristic.

Low-temperature solvothermal synthesis of morphology controlled EuS hollow microspheres

Low-Temperature Solvothermal Synthesis of Eus Hollow Microspheres

Solvothermal Synthesis of Hierarchical Eu2o3 Nanostructures Templated by Ps-B-Pmaa: Morphology Control Via Simple Variation of Water Contents

Solvothermal synthesis of luminescent Eu(BTC)(H 2O)DMF hierarchical architectures

Morphology and Phase Selective Synthesis of EuF3 Nanostructures by Polyelectrolyte Assisted Chemical Reaction and Their Optical Properties

Effect of solvents on morphology and size of US nanoparticles via a solvothermal route

Effect of Solvents on Morphology and Size of CdS Nanoparticles via a Solvothermal Route

Research Progress of Synthesis and Properties of EuS Nanocrystals

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Preparation and Luminescence Properties of Novel 3d Lu2o2s:Eu3+ Microstructures

General and Facile Method To Prepare Uniform Y<sub>2</sub>O<sub>3</sub>:Eu Hollow Microspheres

Controllable Synthesis of EuCO3OH Microspheres and Their Thermal Conversion to Eu2O3

Hydrothermal Synthesis And Photoluminescence Of Eu2-Xsmxsn2o7 (X=0-2.0) Nanophosphors

Synthesis and Luminescent Properties of Monodisperse Core–shell Structured SiO2@Lu2O3:Eu3+ Microspheres

Sacrificial Template Method for Fabrication of Submicrometer-Sized YPO4:Eu3+Hierarchical Hollow Spheres

Facile Synthesis of Monodisperse SrAl2O4:Eu2+ Cage-Like Microspheres with an Excellent Luminescence Quantum Yield

Solvothermal Synthesis of Cds Nanocrystals with Organic Sulphur Source

Highly uniform and monodisperse Gd(2)O(2)S:Ln(3+) (Ln = Eu, Tb) submicrospheres: solvothermal synthesis and luminescence properties

Synthesis and photoluminescence of Eu3+-doped Y2Sn2O7 nanocrystals

Surfactant-free sacrificial template synthesis of submicrometer-sized YVO4:Eu3+ hierarchical hollow spheres with tunable textual parameters and luminescent properties.

Synthesis and Luminescent Modulation of ZnS Crystallite by a Hydrothermal Method