Abstract:Thermal barrier coatings (TBCs) are deposited on metallic components to prevent heat flux due to their excellent thermal insulation function. Nowadays, TBCs have become the key core technology of the new generation gas turbines. TBCs prepared by plasma spraying method are more readily to be failed, which negatively affect the thermal insulation and may cause substrate erosion. Therefore, long life span is an important guarantee for TBCs to achieve thermal barrier function. This paper described the failure mechanism of plasma sprayed TBCs and crack-resistant designs. To begin with, the essential characteristics of plasma sprayed TBCs were revealed. Plasma sprayed TBCs appeared to be lamellar structure with connected 2D pores. As a result, the plasma sprayed TBCs have excellent thermal insulation and strain tolerance at as-deposited state. By thermal exposure, the density of 2D pores is decreased significantly, which dominantly account for the degradation of strain tolerance and thermal insulation. Subsequently, the failure mechanism of plasma sprayed TBCs is revealed. The degradation of strain tolerance leads to increase of driving force for cracking. Consequently, the micro-scale cracks are extended and connected to form large-scale cracks, which is responsible for the failure of plasma sprayed TBCs. Finally, cracking-resistant designs are reviewed from two aspects: decreasing driving force and increasing fracture toughness. It is worth noting that the current cracking-resistant design often has poor performance on thermal insulation. In future research, how to ensure high thermal insulation and long life of the coating while considering the economy is the key direction of the development of a new generation of high-performance thermal barrier coatings.

Progress on heat insulation performance of thermal barrier coatings

Research Progresses in Materials for Thermal Barrier Coatings

Progress in the Deposition Mechanisms and Key Performance Evaluation of Thermal Barrier Coatings for Turbine Blades: A Review

Processing and Advancements in the Development of Thermal Barrier Coatings: A Review

Progress in ceramic materials and structure design toward advanced thermal barrier coatings

Thermal Barrier Coatings on Nickel Superalloy Substrates

Progress Update on Extending the Durability of Air Plasma Sprayed Thermal Barrier Coatings

RESEARCH PROGRESS ON THE EXPERIMENTAL MEASUREMENT METHODS OF MECHANICAL PROPERTIES OF THERMAL BARRIER COATINGS

A comprehensive Review on the Hot Corrosion and Erosion Performance of thermal Barrier Coatings

Research Status of High Entropy Thermal Barrier Coatings: A Review

Multi-Scale Structural Design and Advanced Materials for Thermal Barrier Coatings with High Thermal Insulation: A Review

Present status and prospects of nanostructured thermal barrier coatings and their performance improvement strategies: A review

Novel Low Thermal Conductivity Ceramic Materials for Thermal Barrier Coatings

Thermal Fatigue of Atmospheric Plasma Sprayed Thermal Barrier Coatings

Low-thermal-conductivity thermal barrier coatings with a multi-scale pore design and sintering resistance following thermal exposure

Service Temperature Measurement and Thermal Insulation Mechanism of Thermal Barrier Coatings

Novel Thermal Barrier Coatings with Phase Composite Structures for Extreme Environment Applications: Concept, Process, Evaluation and Performance

Failure Mechanism and Cracking-Resistant Design of Thermal Barrier Coatings with Long Life Span

Thermal barrier coatings (TBC) for energy efficient systems

Research on Thermal Conductivity of Thermal Barrier Coatings

Evaluation and Characterization of a Durable Composite Phase Thermal Barrier Coating in Solid Particle Erosion and Burner Rig Tests