Effect ofη phase powders addition on the microstructure and properties of WC-10Co cemented carbides

Yu GUO,Zhiyou LI,Huiwen XIONG

DOI: https://doi.org/10.3969/j.issn.1673-0224.2016.05.007

2016-01-01

Abstract:WC-Co cemented carbide with plate-like WC grains was prepared by adding 2%, 4%η phase powders and the equimolar carbon black to a ball-milled WC-10Co batch through traditional powder metallurgy process. The carbonization reaction ofη phase, effect of addition amount and the milling time in the batch ofη phase powders on the microstructure and properties of cemented carbide were studied. The results indicate that small additions ofη phase and equimolar carbon black help the development of plate-like grains, the number of plate-like WC grains increases as the amount ofη phase powders increases, and when the total milling time is constant, the distribution of plate-like WC grains is more uniform as the milling time in the batch ofη phase powders increases. This kind of plate-like WC grain is produced from the twined WC which forms from the carbonization reaction between 950℃ to 1 200℃ ofη phase and the C atoms that spread from the matrix, and the carbonization rate ofη phase is the key factor that influence the morphology of twined WC. The density of the cemented carbide with plate-like WC grains is the same as the traditional one which has the equal content of Co, while the hardness, transverse rupture strength, and fracture toughness are increased by 0.7%, 6% and 17%, respectively.