Properties and Cell Activity of Bioceramic Coating Fabricated by Laser Cladding with Different Ca:P Ratios

Bai Yang,Liu Qibin,Xu Peng,Zhu Yizhi,Zhang Shiwei
DOI: https://doi.org/10.13373/j.cnki.cjrm.XY16060014
2017-01-01
Abstract:Due to the difference of thermal expansion coefficient between medical Ti alloy and mixed powder (CaHPO4· 2H2O+Ca-CO3 +La2O3 ) in the process of laser cladding , it was easy to produce cracks , pores and other defects .Therefore, bioactive calcium phosphate coating was prepared on the surface of medical Ti alloy by using gradient design method .The bonding interface , phases, mi-crohardness, bioactivity and cell growth morphology of different n(Ca):n(P) calcium phosphate ceramic coating doped with the same amount of rare earth oxide La2O3 were characterized by optical microscope (OM), X-ray diffraction (XRD), microhardness instru-ment, methyl thiazolyl tetrazolium ( MTT) assay and inverted fluorescence microscope .The experimental results indicated that the cross section of cladding samples observed by OM consisted of substrate , alloying layer and bioceramic coating .There was an excellent metallurgical bonding among layers .When n(Ca):n(P) was 1.40~1.45, the peak of hydroxyapatite +β-Ca3(PO4)2(HA+β-TCP) reached the maximum diffraction intensity at 2θ=32°~33°in the XRD pattern, indicating that mostbiologically active phases β-TCP+HA were synthesized.The microhardness results showed that the higher the n(Ca):n(P) value, the higher the average hardness of the coating was.MTT assay and inverted fluorescence microscope observation results indicated that when n(Ca):n(P) was 1.40, OD val-ue reached the maximum and the relative number of cells on the bioceramic coating was the maximum and the cell growth morphologies were in good condition , indicating that this kind of coating has better biocompatibility and was conducive to the stable proliferation and growth of cells .
What problem does this paper attempt to address?