Abstract:The ductility of metallic materials is recognized to be significantly affected by stress state and strain rate. However, systematic investigations on the impacts of stress state and strain rate on ductile behavior are infrequent, and only a minority of fracture models can consider both effects concurrently. This work aims to systematically investigate the ductile response of Ti6Al4V alloy over a broad spectrum of stress states and strain rates and to propose a ductile model that incorporates the coupled influence of stress state and strain rate. First, five types of specimens were employed to obtain distinct stress states. Then, the fracture strain of material was ascertained for strain rate spanning from 10 −3 /s to 10 3 /s, stress triaxiality ranging from -0.7 to 0.4, and Lode angle parameter varying from -1 to 1 using a combined experimental-numerical method. It was found that over a broad spectrum of stress states, the relation between fracture strain versus stress state is not monotonic, and the fracture strain reduces as strain rate increases. Utilizing the experimental data, a novel ductile fracture model incorporating the stress triaxiality, Lode angle parameter and strain rate was established and embedded into the ABAQUS/Explicit through the user material subroutine VUMAT. Finally, a validation test was conducted to demonstrate the validity of the proposed model. The results indicate the satisfactory correlation between experiment and calculation for fracture displacement and fracture morphology, which illustrates that the proposed model can predict the ductile behavior across a wide spectrum of stress states and strain rates. This work provides a definite theoretical guidance for the optimization design and safety evaluation of Ti-6Al-4V alloy structural components.

Influence of strain path change on material ductile fracture

Coupled effect of stress state and strain rate on ductile fracture of Ti6Al4V alloy

Effects of the stress state on plastic deformation and ductile failure: Experiment and numerical simulation using a newly designed tension‐shear specimen

Prediction of Strain Path Changing Effect on Forming Limits of AA 6111-T4 Based on a Shear Ductile Fracture Criterion

Fracture Prediction under Nonproportional Loadings by Considering Combined Hardening and Fatigue-Rule-based Damage Accumulation

Calibration and Application of Ductile Fracture Criterion under Non-Proportional Loading Condition

A ductile fracture criterion based on stress triaxiality and its application to the shearing process

Study of the Transition from Strain Localization to Fracture of Ti–6.5Al–3.5Mo–1.5Zr–0.3Si Alloy by Experiments and Phase-Field Modeling

Dependence of ductile fracture on stress triaxiality factor

A phase field model for ductile fracture considering the strain rate, stress triaxiality and Lode angle parameter

Ductile Fracture Initiation of Anisotropic Metal Sheets

Research on the ductile fracture criterion in plastic deformation processes

Influence of Stress Triaxiality on Damage and Crack-Tip Opening Displacement Parameters for Steels

Effect of stress triaxiality and normalized Lode angle on ductile fracture of aluminum 2139-T8

Modeling of Shear Ductile Fracture Considering a Changeable Cut-off Value for Stress Triaxiality

Removal of the Influence of Stress Triaxiality on Crack Tip Opening Displacement Fracture Toughness by Continuum Damage Mechanics Approach

Effect of Stress Ratio on the Transition Point of Fatigue Crack Growth Curve in the Near-threshold Regime of a 25cr2ni2mov Steel Welded Joint

Influence of Loading Path on Fatigue Crack Growth under Multiaxial Loading Condition

Fracture of dual phase sheets under uniaxial tension(Ⅱ):Nonlinear finite element analysis

Critical ductile fracture criterion based on first principal stress and stress triaxiality

Evolution of in-plane stresses induced fracture behaviors of Tailor Welded Blanks subjected to non-uniformly distributed load