Hot compression deformation behavior of extruded ZK60 magnesium alloy

Di Zhang,Yunteng Liu,Tao Lin,Jixue Zhou,Zhongkui Zhao

DOI: https://doi.org/10.13251/j.issn.0254-6051.2018.01.007

2018-01-01

Abstract:In order to investigate the hot deformation behavior of extruded ZK 60 magnesium alloy , compression test of the alloy was performed on a Gleebe3-500 thermal simulator at the temperature range of 523-723 K and the strain rate range of 0.01-10 s-1 .The relationship between flow stress and strain rate as well as deformation temperature were analyzed by using the true stress -true strain curves .The constitutive equation for extruded ZK 60 alloy was obtained by introducing the Z parameter .Microstructure evolution of extruded ZK 60 alloy during hot compression deformation was observed .The results show that the true stress-true strain curves of extruded ZK60 alloy is of dynamic recrystallization type , and the flow stress of the alloy is lower at higher deformation temperature and lower strain rate .When the deformation temperature decreases or the strain rate increases , the dynamic recrystallization grain size become finer , but the dynamic recrystallization is not completed and the grain distribution is not uniform .Calculated by the constitutive equation , the deformation activation energy of extruded ZK60 magnesium alloy is Q =122.884 kJ/mol, and the stress exponent is n=5.096.