Abstract:Abstract:A 0.27 mm-thick grain-oriented silicon steel sheet with extra-low carbon was successfully produced by a novel processing route including strip casting, normalizing, two-stage cold rolling with an intermediate annealing, primary annealing, and secondary recrystallization annealing. The evolutions of microstructure and texture along the whole processing route were investigated with a special emphasis on the effects of two-stage cold rolling schedule. It was found that Goss orientation originated in the first cold rolling due to shear banding and relatively strong Goss texture evolved through the whole thickness after intermediate annealing. This is significantly different from the results in conventional process in which the origin of Goss texture is in the hot rolling stage and Goss texture only develops below the sheet surface. Besides, it was found that cold rolling schedule had significant influences on microstructure homogeneity, evolution of λ-fiber texture in primary annealed state and, thus, on secondary recrystallization. In case of appropriate cold rolling schedule, a homogeneous microstructure with Goss texture, relatively strong γ-fiber texture and medium α-fiber texture was observed in the primary annealed strip. Although Goss texture in primary annealed state was much weaker than that in two-stage route in conventional process, a perfect secondary recrystallization microstructure was produced and the magnetic induction B8 was as high as 1.85 T. By contrast, when the cold rolling schedule was inappropriate, the primary annealed strips exhibited inhomogeneous microstructure, together with weak γ-fiber texture, medium α-fiber and λ-fiber texture. Finally, the sheets showed incomplete secondary recrystallization microstructure in which a large number of fine grains still existed.

Effect of hot rolling process on texture of Nb-contained grain-oriented silicon steel after double cold rolling

Effect of hot rolling process on texture of Nb-contained grain-oriented silicon steel after single cold rolling

Effect of Slab Reheating Temperature on Cold Rolling Texture Evolution of Nb-Containing Grain-Oriented Silicon Steel

The effect of Nb content on precipitates, microstructure and texture of grain oriented silicon steel

Effect of Slab Reheating Temperature on Recrystallization Microstructure, Texture and Magnetic Properties of Nb-containing Grain-Oriented Silicon Steel

Micro Characterization of Hot-Rolled Plate of Nb-Bearing Grain-Oriented Silicon Steel

Effect of Nb content on primary recrystallization microstructure, texture and magnetic properties of grain-oriented silicon steel manufactured by low-temperature slab reheating

Evolution of Texture in High Permeability Grain Oriented Silicon Steel Produced by Casting Thin Slab and Rolling Process

Effects of Two-Stage Cold Rolling Schedule on Microstructure and Texture Evolution of Strip Casting Grain-Oriented Silicon Steel with Extra-Low Carbon

Effect of Double Cold Rolling on Magnetic Property and Microstructure of Non-Oriented High Silicon Steel Sheets Cast by Strip Casting Process

EFFECT OF COLD ROLLING PROCESS ON TEXTURE EVOLUTION OF GRADIENT MICROSTRUCTURE IN Fe-3,0 % Si NON-ORIENTED SILICON STEEL

Investigation of microstructure and texture as related to primary recrystallization of grain-oriented silicon steel

Effects of Hot-Rolling Reduction on Microstructure, Texture and Magnetic Properties of High Silicon Steel Produced by Strip Casting

Effect of Cold Rolling Process on Microstructure, Texture and Properties of Strip Cast Fe-2.6%Si Steel

Effect of cold-rolling deformation and rare earth yttrium on microstructure and texture of oriented silicon steel

Effects of hot rolled microstructure after twin-roll casting on microstructure, texture and magnetic properties of low silicon non-oriented electrical steel

Investigation of Primary Recrystallization and Decarbonization with Different Heating Rates of Intermediate Annealing Using Nb-Containing Grain-Oriented Silicon Steel

Effect of Reduction Ratio in Secondary Cold-rolling on Microstructure and Texture of V and Ti-contained Grain-oriented Silicon Steel

Effects of Continuous Rolling and Reversible Rolling on 2.4% Si Non-Oriented Silicon Steel

Effect of Grain Size Before Cold Rolling on Microstructure, Texture and Magnetic Properties of Ultra-Thin Low-Si Non-oriented Silicon Steel

Influence Mechanisms of Cold Rolling Reduction Rate on Microstructure, Texture and Magnetic Properties of Non-Oriented Silicon Steel