Effect of carbon content on microstructure,mechanical properties and intergranular corrosion resistance of 0 Cr25 Ni35 AlTi alloy

Hongxing Deng,Wenjie Zheng,Qihong Cen,Zhigang Song,Han Feng,Lin Wu,Dongyuan Hua

DOI: https://doi.org/10.13251/j.issn.0254-6051.2015.10.003

2015-01-01

Abstract:Effect of carbon content on microstructure, mechanical properties and corrosion resistance of 0Cr25Ni35AlTi alloy steel was investigated. Susceptibility to intergranular corrosion of 0Cr25Ni35AlTi alloy was investigated by means of electrochemical potentiodynamic reactivation. The results show that with the increase of carbon content, the amount of precipitate at grain boundary of alloy increases gradually. The content of Cr-rich M23 C6 as the dominant precipitates increases from 0. 186% to 0. 499%;the tensile strength increases form 686. 5 MPa to 714 MPa at room temperature. With increase of carbon content, the average grain size decreases, the amount of M23 C6 precipitation increases, mechanical properties are improved, and however, intergranular corrosion resistance deteriorates obviously. It can be concluded that carbon content of the alloy should be controlled at about 0. 025%, making it has a good resistance to intergranular corrosion and still strength higher than 300 MPa so that meet the mechanical properties requirement.