Testing of Thin Laminated Composite Plate with Ultrasonic Feature Scan Imaging System

LU Ming-hui,FU De-yong,WANG Hai-fang,LI Qing,WANG Shu-shuang,CHEN Yi-fang

DOI: https://doi.org/10.3969/j.issn.1000-6656.2005.09.001

2005-01-01

Abstract:Conventional ultrasonic imaging methods such as B-scan and C-scan couldn't meet the requirements of composite inspection. A new ultrasonic imaging method, feature scan (F-scan) imaging, was introduced including its inspecting principle, scanning system design and focusing transducer manufacture and so on. In the method of F-scan imaging, ultrasonic waveform features (i.e. rising and falling time, pulse period and frequency spectrum) and defect features (i.e. the type, shape and size of defects) were taken as characteristic quantity to acquire and reconstruct the signals received, and finally to make imaging. The laminated composite thin plate with thickness of 2 mm was taken as testing sample, in which three lamination defects with diameter not less than  1.2 mm were made on the binding layers at 0.6 mm and 1.4 mm from the upper surface of the composite plate respectively. It was shown by experimental results that the prepared defects were successfully detected by the ultrasonic feature scanning system designed with various imaging modes (e.g. amplitude imaging, depth imaging and bottom wave imaging). The designed system had an additional function of computed tomography, and could also be used for the imaging of both the density of thin laminated plate and the thickness of hard alloys. Based on its special and effective function, ultrasonic feature scan imaging method would find wide application in material analysis.