Effect Of Ti Addition On The Microstructure And Wear Properties Of Alfecrcocu High-Entropy Alloy

Xie Hongbo,Liu Guizhong,Guo Jingjie,Zhou Min,Liu Depiao,Mao Weiqian
2016-01-01
Rare Metal Materials and Engineering
Abstract:The microstructures of AlFeCrCoCu, AlFeCrCoCuTi and 800 degrees C tempered AlFeCrCoCuTi high-entropy alloys fabricated by an arc remelter were investigated by XRD, SEM, EDS and DSC. The alloys' hardness and wear properties were also tested. The results show that AlFeCrCoCu alloy possesses face-centered cubic (fcc) and body-centered cubic (bcc) phases. After the addition of titanium, AlFeCrCoCuTi alloy is composed of primary dendrite phase (The beta phase rich in Al, Co, Ti and the a phase rich in Fe, Cr eutectoid structure), interdendrite phase rich in Cu and the precipitated phase rich in Cr. Meanwhile, the hardness of AlFeCrCoCuTi alloy increases. AlFeCrCoCuTi alloy exhibits a superior resistance to tempering and softening. The wear of the three alloys is adhesive wear, while the wear resistance of the AlFeCrCoCuTi alloy improves, and the wear resistance of 800 degrees C tempered AlFeCrCoCuTi alloy is better than that of as-cast alloys. The main reason is that with the increase of friction time, the 800 degrees C tempered AlFeCrCoCuTi alloy generates a layer of oxide on the surface and it attaches to the friction surface, thus improving the wear resistance of the alloy.
What problem does this paper attempt to address?