Effect of Austenitizing Temperature on Microstructure and Properties of DGJW30 Steel-bonded Carbide

Aijun LIU,Ning LIU,Xinjie CHENG,Hongliang ZHANG

DOI: https://doi.org/10.3969/j.issn.1008-1690.2014.04.007

2014-01-01

Abstract:The electromelted and cast DGJW30 steel-bonded carbide was heat treated and subjected to microstructure survey by means of OM,SEM,EDS,and XRD.The effect of austenitizing temperature on the microstructure,hardness and bending strength of the DGJW30 carbide was investigated.The results show that matrix structure of as-quenched DGJW30 carbide is crypto-crystalline martensite,and that the hard phase contains both the undissolved tungsten carbide and recrystallized carbide.Besides,as the austenitizing temperature rises up to 1050 ℃ hardness of the DGJW30 carbide increases and,however,the quenching from still temperature of 1 100 ℃ will render hardness of the DGJW30 carbide much lower.The bending strength increases progressively with the elevation of the austenitizing temperature up to 1 100 ℃.