Abstract:The corrosion resistance and discharge activity of the rolled A represents aluminum, Z represents zinc, 9 and 1 represent their respective contents of 9% and 1% in the alloy magnesium alloy after electric pulse treatment show obvious patterns. Through research on its patterns and causes through immersion weight loss and electrochemical testing combined with microstructure observation results, it is found that the β‐Mg17Al12 phase and high‐energy grain boundary area in the alloy play a key role. In this article, a systematic investigation into the corrosion and discharge behaviors of as‐rolled a represents aluminum, Z represents zinc, 9 and 1 represent their respective contents of 9% and 1% in the alloy (AZ91) magnesium alloy after electro pulsing treatment (EPT), considering rolling deformations of 0% (as‐cast AZ91 magnesium alloy), 20%, 30%, and 40%, is presented. In this investigation, immersion weight loss tests, electrochemical tests, and other experimental methods are employed. In the results, it is revealed that the content of the β‐Mg17Al12 phase gradually decreases with increasing rolling deformation after EPT. Notably, the highest content of β‐Mg17Al12 phase and the most outstanding corrosion resistance are achieved with as‐cast AZ91 magnesium alloy. Furthermore, at low current densities (5 and 10 mA cm−2), the 30% rolling deformation exhibits superior discharge activity, while the discharge activity of the 40% rolling deformation is most excellent at high current densities (40 and 50 mA cm−2). The microstructure observations support these findings, highlighting the close relationship between the corrosion resistance and discharge activity of as‐rolled AZ91 magnesium alloy after EPT, and the content of the β‐Mg17Al12 phase and the area of high‐energy grain boundaries.

Application Study of High Energy Pulse Current in Rolling of AZ31 Magnesium Alloy

Enhanced Rollability of Mg-3al-1zn Alloy by Pulsed Electric Current: A Comparative Study

Effect of electric pulse rolling on plastic forming ability of AZ91D magnesium alloy

Research of Electroplastic Rolling of Az31 Mg Alloy Strip

Influence of Thermo-Electropulsing Rolling Process on Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Strip

Recrystallization and Anisotropy of AZ31 Magnesium Alloy by Asynchronous Rolling

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Effect of Electric Pulse‐Assisted Extrusion on the Dynamic Recrystallization and Mechanical Properties of AZ31 Alloy

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Inhibition Behavior of Edge Cracking in the AZ31B Magnesium Alloy Cold Rolling Process with Pulsed Electric Current

Microstructure and texture evolution of cold-rolled Mg-3Al-1Zn alloy by electropulse treatment stimulating recrystallization

Obtaining Heterogeneous Microstructure and Enhanced Mechanical Properties in ECAP-Processed AZ61 Alloys via Single-Pass Rolling with Increased Rolling Reduction

Corrosion and Discharge Behavior of As‐Rolled AZ91 Magnesium Alloy after Electro‐Pulsing Treatment

Athermal influence of pulsed electric current on the twinning behavior of Mg-3Al-1Zn alloy during rolling

Design high-performance AZ31 ultrathin strip through multi-pass electroplastic rolling without off-line annealing

Effects of Rolling-Cryogenic Process on Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets

Mg–3Al–1Zn alloy strips processed by electroplastic differential speed rolling

Microstructure and Texture Evolution of Magnesium Alloys During Electropulse Treatment

Achieving single-pass high-reduction rolling and enhanced mechanical properties of AZ91 alloy by RD-ECAP pre-processing

Enhanced mechanical properties of AZ91 magnesium alloy by asynchronously large-strain high-efficiency rolling with bimodal grain structure

Influence of Microstructure and Mechanical Properties on Formability in High Strain Rate Rolled AZ31 Magnesium Alloy Sheets