Cold Sintering Assisted Processing of Mn-Zn Ferrites
Mingming Si,Xinyi Li,Changli Fu,Xian Xue,Xiaomeng Li,Fuliang Wang,Shouqiang Han,Jing Guo
DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.06.013
IF: 5.7
2023-06-09
Journal of the European Ceramic Society
Abstract:Typically, commercial Mn-Zn ferrites are sintered at high temperatures with prolong times. In this work, commercial Fe 2 O 3 -rich ferrite powders with the composition of 0.21Mn 0.8 Zn 0.2 Fe 2 O 4 -0.79Fe 2 O 3 (wt%) are densified by cold sintering at 300 °C with the assistance of organic salts, including MnC 2 O 4 ·2H 2 O, FeC 2 O 4 ·2H 2 O, and Zn(C 2 H 3 O 2 ) 2 ·2H 2 O. Excessive Fe 2 O 3 enters into spinel structure forming a solid solution through annealing in low p O 2 at 1350 °C. The sintering behaviors, microstructures, magnetic properties and impedances are investigated. The dehydration of organic salts provides mediate liquid phase to trigger the dissolution-precipitation process, which assists the densification of ceramics. The grains grow from 0.15 μm to 0.52 μm and 7.67 μm after cold sintering at 300 °C and annealing at 1350 °C, respectively. The initial permeability of cold sintered sample is improved to 11000 with a Curie temperature of 125 °C. This work provides a feasible route for cold sintering assisted processing of commercial soft magnetic ferrites.
materials science, ceramics