Abstract:The temperature enduring capacity of turbine blades determines the thrust-weight ratio of aero-engines. The heat dissipation efficiency of blades is improved mainly through designing complex internal cooling channel. As a transitional component of blade preparation, the shape of ceramic cores has become gradually complex. The traditional process is difficult to meet the preparation requirements of ceramic core with complex structure due to the limitation of mold. Stereolithography 3D printing provides a feasible technology for the preparation of ceramic cores with complex structures. The key to high-performance ceramic core via the stereolithography 3D printing lies in the prepare ceramic slurry with high solid loading, low viscosity and uniform stability. Choosing suitable dispersant is an effective way to prepare above standard slurry. In this study, the effects of single and dual dispersants on the rheological properties of ceramic slurry were systematically investigated. The action mechanism of the dispersant was analyzed. The functional relationship between solid loading and viscosity was elucidated. The silicon-based ceramic core slurry with 70 vol% solid loading and viscosity of 10520 mPa s (12.6 s−1) was obtained. Through optimizing printing parameters, the complex structure silicon-based ceramic core was fabricated. The influence of solid loading on the microstructure and physical properties of the ceramic core was investigated. The results show that with the increase of solid loading, the shrinkage of ceramic core lowers and the flexural strength of ceramic core strengthens. The successfully preparation of complex structure ceramic core based on high solid loading slurry promotes the extensively implemented of stereolithography 3D printing technology in the field of ceramic core.

Defects Control of Manufacturing Ceramic Mold of Hollow Turbine Blade Based on Stereo Lithography

The Method of Stereo Lithography Prototype Inner Cavity Structure Design for Increasing Hollow Blade Mold Accuracy

Design and Fabrication of Stereolithography-based Integral Ceramic Molds for Gas Turbine Blades

The Preparation Of Calcia-Based Ceramic Slurry For Rapid Manufacturing Hollow Turbine Blade Based On Stereolithography

Fabrication of Integral Ceramic Mold for Investment Casting of Hollow Turbine Blade Based on Stereolithography

Rapid Casting of Hollow Turbine Blades Using Integral Ceramic Moulds

Rapid Casting of Turbine Blades with Abnormal Film Cooling Holes Using Integral Ceramic Casting Molds

Fabrication of Integral Core/Shell Ceramic Casting Mould for Hollow Turbine Blade

Direct Fabrication of an Integral Ceramic Mould by Stereolithography

A Way to Resolve Crack Defects of Ceramic Mold Core

Numerical Study of the Pore Defects Formation Mechanisms in Selective Laser Melting Process

Ceramic shell fabrication via Stereo Lithography Apparatus: Recent progress on cracking problems and preventive measures

Elimination of the Stray Grain Defects of Single Crystal Blade by Variable Wall Thickness Based on Integral Ceramic Mold

Enhanced Crack Resistance in Ceramic Shells Fabricated with Photosensitive Resin Models Printed by Stereolithography Through Buffer Layer Integration

Rapid Casting of Hollow Turbine Blades with Converging-Expanding Film Cooling Holes

Quick Fabrication of Aeronautical Complicated Structural Parts Based on Stereolithography

Analysis of Ceramic Shell Cracking in Stereolithography-Based Rapid Casting of Turbine Blade

Application study of new mould-parting technology of ceramic core mould to turbine blade

Rapid fabrication of alumina-based ceramic cores for gas turbine blades by stereolithography and gelcasting

High solid loading, low viscosity stereolithography 3D printing ceramic cores slurry

On the Defects in Injection-Moulded Technical Ceramics