Influence of current density on microstructure and corrosion resistance of micro-arc oxidation films on Al-Si alloy

Chuang LU,Faqin XIE,Liping ZHU,Guoxiao LIU

DOI: https://doi.org/10.14024/j.cnki.1004-244x.20170706.002

2017-01-01

Abstract:Micro-arc oxidation (MAO) was used to prepare the coatings on the surface of Al-Si alloy.The laser scanning confocal microscope (LSCM),scanning electron microscope (SEM),energy dispersive spectrometer(EDS),X-ray diffraction (XRD) and electrochemical polarization curve were utilized to study the influence of current density on the growth process,themicrostructure characteristics,the components distribution,and the phase compositions,the corrosion resistance of the microarc oxidation coatings on Al-Si alloys.The results show that with the increase of current density,the arc time shortens,the film thickness and surface roughness increase,the film growth rate increases first and then decreases.When the current density is low,the MAO film is mainly consisted of γ-A12O3.When the current density increases to 13.3 A/dm2,the MAO film is mainly consisted of γ-Al2O3、αt-Al2O3 and mullite phase.When the current density is less than 16.6 A/dm2,thecorrosion resistances of the MAO films improve with the current density increasing.When the current density is larger than 16.6 A/dm2,the corrosion resistance of MAO film decreases with the current density increasing.Compared with matrix alloy,the passivation current density of the MAO film reduces by two orders of magnitude.