Preparation of sulfydryl functionalized magnetic SBA-15 by an assembling process

Yaping ZHANG,Bin ZHEN,Hansheng LI,Yaqing FENG

DOI: https://doi.org/10.16085/j.issn.1000-6613.2017-1294

2018-01-01

Abstract:Monodisperse and magnetic manganese ferrite nanoparticles with average diameter of 15nm were synthesized by a thermal decomposition method. The obtained magnetic nanoparticles were anchored onto the surface of SBA-15 through ligand exchange reaction of oleic acid and tetraethylorthosilicate. Meanwhile,sulfydryl functionalized magnetic SBA-15 was prepared by combining the anchoring process and surface modification of SBA-15. The influence of drying methods used during the synthesis of SBA-15 on its structure and properties was investigated. Effect of execution sequence of the anchoring and modification process on the structure and properties of sulfydryl functionalized magnetic SBA-15 was discussed. The result showed that SBA-15 prepared by spray drying showed thinner pore wall,higher specific surface area,pore volume and larger pore diameter,and could support more magnetic nanoparticles and thus exhibited stronger saturation magnetization. When the anchoring of the magnetic nanoparticles occurred on surface of the modified SBA-15,more nanoparticles were anchored on the surface of the SBA-15 due to a compatible hydrophobic chemical environment. Magnetic nanoparticles were mainly anchored onto the outside surface of SBA-15 because the pore diameters of the SBA-15 were smaller,which conserved the mesopores of SBA-15 unblocked. The obtained sulfydryl functionalized magnetic SBA-15 had pore volumes between 0.56cm3/g and 0.6cm3/g,specific surface area between 353m2/g and 432m2/g,and saturation magnetization of 0.91emu/g,which make it a high-capacity adsorbent for separation and drug release.