Abstract:This paper describes a solution-phase synthesis of high-quality vanadium dioxide thermochromic thin films. The films obtained showed excellent visible transparency and a large change in transmittance at near-infrared (NIR) wavelengths before and after the metal-insulator phase transition (MIPT). For a 59 nm thick single-layer VO(2) thin film, the integral values of visible transmittance (T(int)) for metallic (M) and semiconductive (S) states were 54.1% and 49.1%, respectively, while the NIR switching efficiencies (DeltaT) were as high as 50% at 2000 nm. Thinner films can provide much higher transmittance of visible light, but they suffer from an attenuation of the switching efficiency in the near-infrared region. By varying the film thickness, ultrahigh T(int) values of 75.2% and 75.7% for the M and S states, respectively, were obtained, while the DeltaT at 2000 nm remained high. These results represent the best data for VO(2) to date. Thicker films in an optimized range can give enhanced NIR switching efficiencies and excellent NIR blocking abilities; in a particularly impressive experiment, one film provided near-zero NIR transmittance in the switched state. The thickness-dependent performance suggests that VO(2) will be of great use in the objective-specific applications. The reflectance and emissivity at the wavelength range of 2.5-25 microm before and after the MIPT were dependent on the film thickness; large contrasts were observed for relatively thick films. This work also showed that the MIPT temperature can be reduced simply by selecting the annealing temperature that induces local nonstoichiometry; a MIPT temperature as low as 42.7 degrees C was obtained by annealing the film at 440 degrees C. These properties (the high visible transmittance, the large change in infrared transmittance, and the near room-temperature MIPT) suggest that the current method is a landmark in the development of this interesting material toward applications in energy-saving smart windows.

Application advances of vanadium dioxide in infrared camouflage and stealth technology

Thermal-stimulated Phase Transition of Vanadium Dioxide Enabling Versatile Transduction and Smart Applications

Vanadium dioxide nanopowders with tunable emissivity for adaptive infrared camouflage in both thermal atmospheric windows

Vanadium Dioxide/aluminum Composites for Adaptive Infrared Stealth

Recent advances in vanadium dioxide for dynamic thermal radiation modulation: A review

Research Progress on Thermochromic Properties of Vanadium Dioxide Thin Films for Smart Windows

One-Step Hydrothermal Synthesis, Thermochromic and Infrared Camouflage Properties of Vanadium Dioxide Nanorods

Infrared optical modulation characteristics of W-doped VO2(M) nanoparticles in the MWIR and LWIR regions

Enhanced passive thermal stealth properties of VO$_2$ thin films via gradient W doping

Recent Progress in VO2 Smart Coatings: Strategies to Improve the Thermochromic Properties

Infrared thermochromic properties of monoclinic VO2 nanopowders using a malic acid-assisted hydrothermal method for adaptive camouflage

Bioinspired Multifunctional Vanadium Dioxide: Improved Thermochromism And Hydrophobicity

A universal approach to fabricating infrared-shielding smart coatings based on vanadium dioxide

10.6Μm Infrared Light Photoinduced Insulator-to-metal Transition in Vanadium Dioxide

Simultaneous tuning of the phase transition temperature and infrared optical properties of Mo-doped VO2 powders for intelligent infrared stealth materials

Dual-phase change composites with temperature control and low infrared emissivity properties fabricated by electrospinning for infrared stealth and thermal camouflage

Infrared Chameleon-Like Behavior from VO2(M) Thin Films Prepared by Transformation of Metastable VO2(B) for Adaptive Camouflage in Both Thermal Atmospheric Windows

Thermochromic VO2 thin films: solution-based processing, improved optical properties, and lowered phase transformation temperature

Largely Lowered Transition Temperature of a VO2/Carbon Hybrid Phase Change Material with High Thermal Emissivity Switching Ability and Near Infrared Regulations

W/Al Co-doping VO2 Nanoparticles for High Performance Passive Infrared Stealth Films with Enhanced Durability

Infrared Transition Properties of Vanadium Dioxide Thin Films Across Semiconductor-Metal Transition