Abstract:Thermal transition temperatures (e.g. glass transition temperatures) play an important role in various applications of shape memory polymers that can recover from temporary shapes to original (permanent) shapes upon heating. This study reports a shape memory epoxy with unsaturated double bonds, enabling a secondary photocuring process. Dual-functional epoxy monomer, E44, and monofunctional epoxy monomer, glycidyl methacrylate, are first thermally cured via a polyether amine crosslinker. Properties of the cured epoxy can be finely tuned by controlling the feed compositions. The increase of feed ratio of glycidyl methacrylate will lead to lower glass transition temperature and elastic modulus, whereas larger strain at break. In the secondary photocuring process, the unsaturated bonds provided by glycidyl methacrylate are polymerized after light exposure, forming additional crosslinking points. As a result, the glass transition temperature of the material increases. Herein, digital photo-masking technique is applied for the photocuring process via a commercial projector. The regional exposure time of the material can be conducted, and thus, the local glass transition temperature can be controlled in a range of approximately 40 - 70 degrees C. Storage modulus at the rubbery state of the material increases from approximately 0.5 MPa to 8 MPa after photo exposure for 240 s, implying that there is a remarkable increase of the crosslinking density via the secondary photocuring. Both the materials before and after the secondary photocuring provide ideal shape memory performance. The shape fixity ratios and shape recovery ratios retain nearly 100% during six shape memory cycles, indicating good thermo-mechanical stability of the material. The material with regional controllable glass transition temperature enables a programmable multi-shape recovery process. Complex original shapes can be fabricated if the secondary photocuring is conducted towards a thermally cured epoxy. In addition, the material can be potentially applied as a novel substrate for stretchable electronics due to its strain isolation functionality.

Multi-Shape Memory Liquid Crystal Polymers

Shape Memory Polymers with Regionally Defined Glass Transition Temperature via Digital Photocuring

Revealing Triple-Shape Memory Effect by Polymer Bilayers.

Solvent-driven temperature memory and multiple shape memory effects.

Multishape Memory Effect of Norbornene-Based Copolymers with Cholic Acid Pendant Groups

Tunable Polymer Multi-Shape Memory Effect

Deformable, Programmable, and Shape-Memorizing Micro-Optics

A Metallosupramolecular Shape‐Memory Polymer with Gradient Thermal Plasticity

Shape Memory Behaviors of 3D Printed Liquid Crystal Elastomers

Synergetic Chemical and Physical Programming for Reversible Shape Memory Effect in a Dynamic Covalent Network with Two Crystalline Phases

Significant Impact of Thermo-Mechanical Conditions on Polymer Triple-Shape Memory Effect

Triple-shape Memory Effect in 3D-Printed Polymers

Semi-crystalline Two-Way Shape Memory Elastomer

Shape Memory Polymer Network with Thermally Distinct Elasticity and Plasticity

Shape-Memory Polymers with Multiple Transitions: Complex Actively Moving Polymers

Omnidirectional Shape Memory Effect Via Lyophilization of Peg Hydrogels

Core-Shell Nano-Latex Blending Method to Prepare Multi-Shape Memory Polymers

A New Strategy to Prepare Polymer Composites with Versatile Shape Memory Properties

Triple-shape memory effects of bismaleimide based thermosetting polymer networks prepared via heterogeneous crosslinking structures

A general approach towards thermoplastic multishape-memory polymers via sequence structure design.

Regulation of Glass Transition Temperature in Thermo‐Responsive Epoxy Shape Memory Polymers: The Roles of Chemical Crosslinking Density and Chain Flexibility