Study on Microcellular Foaming of CTBN Toughened Epoxy Resin

Xun Fan,Guangcheng Zhang,Jiantong Li,Hongming Zhang

DOI: https://doi.org/10.3969/j.issn.1001-3539.2017.04.011

2017-01-01

Abstract:The conditions and cell structures of microcellular foams using supercritical carbon dioxide (SC–CO2) technology based on high molecular weight epoxy resin (CYD–014U) modified with carboxyl-terminated butadiene-acrylonitrile copolymer (CTBN) were researched. Differential scanning calorimeter (DSC),dynamic thermal mechanical(DMA) and scanning electron microscope (SEM) were used to analyze the thermal property,dynamical modulus and morphologies of fracture surface and cells. It is found that as the contents of CTBN increases the temperature of glass transition measured by DSC persistently decreases,from 98.44 ℃ to 81.89 ℃ . SEM fracture surface shows plastic deformation of epoxy resin matrix and rubber phase separation appears when CTBN concentration increases. The CO2 absorbed concentration improves and desorption speed accelerates as rubber contents increases. The cell diameter and cell density are from 1 μm and 5.60×1010 cells/cm3 to 2 μm and 6.28×1010cells/cm3 during the 10%–15% CTBN concentration when the samples are placed in autoclave at 60 ℃,12 MPa,72 h and foams 10 s to 15 s at 110℃ . For the epoxy resin toughed with 15% CTBN,as foaming time is up,the bubble periods can be divided into cell nucleation, cell growth and cell collection,and it can be concluded that the cell diameter is increased and the cell density is fimproved and then reduced.