Effects of Particle Sizes of Organic Phosphate Nucleating Agent on PP Properties

张恰,赵世成,石尧麒,辛忠,周帅

DOI: https://doi.org/10.3969/j.issn.1001-3539.2016.07.004

2016-01-01

Abstract:Sodium 2,2’-methylene-bis-(4,6-di-t-butylphenylene) phosphate (NA–40) nucleating agents with different particle sizes were produced by controlling rotation rate,sovent/anti-solvent ratio and solution concentration through antisovent method. The effects of particle size on isotactic polypropylene (iPP) crytalization properties and mechanical properties were studied. The re-sults shows that mechnical properties are impoved with the decrease of nucleating agents particle sizes. When the nucleating agent average particle size is (17.7±2.2)μm,the flexural modulus,flexural strength and tensile strength of iPP are impoved by 44.5%, 20.5% and 8.3% respectively,compared with pure iPP. When the nucleating agent average particle size is (52.6±1.1)μm,the flexural modulus,flexural strength andtensile strength of iPP are impoved by 16.8%,2.3%和6.4% respectively. The influence of nucleating agents particle is not obvious unless the cooling rate reach a certain level. Observing NA–40 with SEM,which shows a bars-like morphology. The anti-solvent processing did not changed the morphology of NA–40 except for particle size. using POM to study the dispersity of NA–40 in iPP,and the results shows that NA–40 with smaller particle size disperse well in iPP,while those with larger size cannot disperse very well,which may greatly reduce the effective concentration of NA–40 and affect NA–40 on the improvement of the mechanical properties and crystallization behaviors of iPP.