Preparation and performance characteristic of MAPP flame-retardant EVA foamed composites

Hanqing LIAN,Yuying ZHENG,Hongfeng QIU
DOI: https://doi.org/10.11949/j.issn.0438-1157.20151597
2016-01-01
Abstract:The MAPP, as a derivative of ammonium polyphosphate (APP), was synthesized via a grafting reaction between APP and ethylenediamine (EDA). The intumescent flame-retardant was fabricated by the mixture of MAPP, EG, and WF, and introduced into the EVA matrix for the preparation of flame-retardant EVA foamed composites. The FT-IR, XRD, 1H NMR, LOI, UL-94, CONE, SEM, TG, and electronic universal testing machine were applied to appraise the grafting degree, flame-retardant, and mechanical performance of the as-obtained composites, respectively. The results showed that the EDA has been successfully grafted on APP, and the as-prepared MAPP could not only possess desirable flame-retardant performance, water-resistance, as well as a better compatibility with EVA matrix, but also decrease the heat release. It is worth noting that foamed composite obtained the optimum comprehensive properties when the MAPP loading was 20%, and exhibited 28.8% (LOI), V-0 (UL-94), 1.282 MPa (tensile strength), and 326. 40% (elongation), respectively.
What problem does this paper attempt to address?