Synthesis and characterization of hydrophobic associating acrylamide-based copolymer with double-tailed hydrophobic monomer

Feng JIANG,Wanfen PU,Daijun DU,Qiang REN,Xueqi JING

DOI: https://doi.org/10.11949/j.issn.0438-1157.20140880

2015-01-01

Abstract:In order to improve salt resistance, temperature tolerance and stability of the acrylamide-based copolymer, the hydrophobic associating copolymer (DTHAP) of acrylamide (AM) with acrylic acid (AA) and a double-tailed hydrophobic monomer (N-phenethyl-N-tetradecylmethacrylamide, PETMAM) was synthesized by photo-initiated radical polymerization. By measuring apparent viscosity of the hydrophobic associating polymer, the effects of amounts of acrylic acid, salt, surfactant (SDS) and content of the double-tailed hydrophobic monomer on the properties of the copolymer were investigated. The critical associating behavior of the copolymer could be affected by changing the amounts of surfactant and acrylic acid. Then, the amount of surfactant could be reduced by adding NaCl to the solution in the micellar polymerization process. Finally, even at low concentration [0.35%—0.45%(mol)] of hydropobic monomer, the copolymer could exhibit obvious thickness. For the hydrophobic associating copolymer synthesized, its critical association mass concentration was about 0.75 g·L?1 and its viscosity was 141.5 mPa·s at the concentration of 1 g·L?1. After ageing for 90 d at 80℃, the apparent viscosity of 2 g·L?1 DTHAP in 120 g·L?1 NaCl solution was 47.6 mPa·s. Even in 120 g·L?1 NaCl and 0.4 g·L?1 CaCl2 solution, the viscosity of the copolymer solution could be kept at around 45.9 mPa·s. The copolymer was characterized with FTIR and SEM, and its structure was confirmed.