Effect of Silica on Ceramifying Properties of Silicone Rubber-based Ceramizable Composites

Han-jian LI,Jian-hua GUO,Wei GAO,Xing-rong ZENG

DOI: https://doi.org/10.11941/j.issn.1009-4369.2015.05.002

2015-01-01

Abstract:The effects of variety and contents of silica on the properties of ceramizable silicone rubber, such as three point flexural strength, compressive strength, weight loss percentage and percent of linear shrinkage, were investigated, whose fracture surface was analyzed by SEM. It is shown that the ceramizable silicone rubber added with fumed silica has higher flexural strength and compressive strength, higher percent-age of linear shrinkage, more compact fracture surface and better ceramifying effects than that added with pre-cipitated silica. The three point flexural strength and compressive strength of the ceramics increases, the per-centage of weight loss and linear shrinkage decreases, and its ceramic surface shows a few bubbles and the in-ner compactness with the increasing silica. With the addition of 40 phr fumed silica, the ceramics show the maximum flexural strength and the maximum compressive strength with the values of 14. 1 MPa and 6. 0 MPa, respectively, as well as the minimum weight loss percentage and the minimum percent of linear shrinkage of 37. 6% and 2. 8%, respectively.