Abstract:A novel bio-based benzoxazine resin (phenolphthalein-furfuramine-benzoxazine , PTL-F-BOZ) , used bio-based furfurylamine , phenolphthalein , and paraformaldehyde as raw materials , was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) , nuclear magnetic resonance (H-1 NMR and C-13 NMR) . The curing , thermal and flame retardant properties were analyzed by differential scanning calorimetric (DSC) , thermogravimetric analyzer (TG) , limiting oxygen index (LOI) , vertical burning test, microscale combustion calorimetry (MCC) , cone calorimeter(Cone) and scanning electron microscope (SEM) . The DSC curve of PTL-F-BOZ showed a two-stage curing with two maxima at 224 and 251 degrees C respectively, and had lower curing temperature than that of the traditional fossil-based bisphenol benzoxazine bisphenol A-aniline benzoxazine (bisphenol A-aniline-benzoxazine , BPA-A-BOZ) . The presence of the furan ring in the furfurylamine increased the cross-linking density of polymer, retarded the rearrangement reaction from the phenoxy structure to the phenol structure, and resulted in two curing peaks in the DSC curve of PTL-F-BOZ. Under nitrogen and air atmospheres, the temperatures of 5% mass loss (T-5%) for PPTL-F-BOZ resin were 380 and 370 degrees C , respectively and the residual chars at 800 degrees C were 63. 0% and 10. 5% , respectively. Compared with PBPA-A-BOZ resin, PPTL-F-BOZ resin both possessed higher T-5% and residual char of 800 degrees C. From the DTG curve , the maximum mass loss rates of two decomposition stage (Peak 1 and Peak 2 values) of PPTL-FBOZ resin were 0. 67%/min and 3. 28%/min, which were only 7. 38% and 63. 44% of PBPA-A-BOZ (9. 07%/min and 5. 17%/min) under nitrogen atmosphere , and those were also the same under air atmosphere. LOI of PPTL-F-BOZ resin was 36. 2%, which was higher than that of PBPA-A-BOZ resin. Meanwhile, in the UL-94 test, PPTL-F-BOZ resin extinguished quickly and released less smoke during combustion process, and the original morphology was kept well and a stable carbon layer was formed after burning. Its first ignition time(t(1)) and second ignition time(t(2)) were 1. 4 and 8. 5 s , respectively , far smaller than the maximum permissible values of 10 s, and a UL94 V-0 rating was also achieved. Hence, PPTL-F-BOZ resin showed excellent thermal and flame retardant properties.

Synthesis of bisphenol F from polyoxymethylene dimethyl ethers

Oxidation of Bisphenol F (BPF) by Manganese Dioxide

Selective Synthesis of Bisphenol F from Phenol and PODE2 over an Acidic Resin–Carbon Composite Material

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis and Properties of a Novel Bio‐based Benzoxazine Resin with Excellent Low‐temperature Curing Ability

Decomposition of polyoxymethylene dimethyl ethers and synthesis of bisphenol F

Synthesis and Properties of a Novel Bio-based Benzoxazine

Tuning Bis(imino)pyridyl Iron‐Catalyzed Ethylene Oligomerization by Modification of MAO with P‐brphoh

Kinetics of synthesis of polyoxymethylene dimethyl ethers from paraformaldehyde and dimethoxymethane catalyzed by ion-exchange resin

Identification of the Rate-Determining Step for the Synthesis of Polyoxymethylene Dimethyl Ethers from Paraformaldehyde and Dimethoxymethane

Bisphenol F Synthesis from Formaldehyde and Phenol over Zeolite Y Extrudate Catalysts in a Catalyst Basket Reactor and a Fixed-Bed Reactor

OXIDATIVE POLYMERIZATION BEHAVIOR OF 2,6-DIMETHYLPHENOL IN AQUEOUS MEDIA WITH POTASSIUM FERRICYANIDE

Mechanism of Chain Propagation for the Synthesis of Polyoxymethylene Dimethyl Ethers

Polymer-based solid acids with adjustable textural and hydrophobic properties for polyoxymethylene dimethyl ethers synthesis from formaldehyde and methanol

A Novel Synthetic Method for Preparing Poly(2,6-Dimethyl-1,4-phenylene Oxide)/polystyrene Alloy in Reactor Containing Aqueous Medium

Study on Synthesis of 2,2-Bis[4-(2-hydroxyethoxy)phenyl]propane in Di-butyl Ether

Polymerization of 2,6-Dimethylphenol by Oxidative Coupling Mechanism in Aqueous Medium

Molecular Size Distribution in Synthesis of Polyoxymethylene Dimethyl Ethers and Process Optimization Using Response Surface Methodology

Synthesis and Characterization of Α,ω-Bis(2,6-dimethylphenol)-poly(2,6-dimethyl-1,4-phenylene Oxide) Oligomers in Water and the End-Group Modification

Effects of water and methanol on synthesis of polyoxymethylene dimethyl ethers from dimethoxymethane and paraformaldehyde

Optimization of preparation techniques for high-temperature resistant waterborne phenolic-epoxy resin emulsion under low carbon background