Effect of ionic surfactants on the morphology of PS-b-PAA block copolymers in DMF/H2 O mixtures

Man XI,Tian-hao ZHANG,Bo LIANG,Bao-yan ZHANG

DOI: https://doi.org/10.16581/j.cnki.issn1671-3206.2014.07.011

2014-01-01

Abstract:Two glycerol-based surfactants which had similar structures but oPPosite charge were synthe-sized. The cationic surfactant was N,N-dimethyl-N-(2-oxo-2-((16,16,26,26-tetramethyl-18,24-dioxo-19 ,23-dioxa-16 ,26-diazadotetracontan-16 ,26-diium-21-yl )oxy )ethyl )hePtadecan-1-aminium chloride ( named S1 ),whereas the anionic surfactant was 2-( Palmitoyloxy )malonate disodium salt( named S2 ). The influences of S1 and S2 addition on the self-assembly behavior of Polystyrene-b-Poly( acrylic acid) ( PS-b-PAA)in DMF/H2 O mixtures were investigated. The result showed that both cationic and anionic surfactants can interact with the coPolymer,inducing the morPhological transition. As the concentrations of S1 increased,the aggregates morPhology changed from short rods to longer rods,and from longer rods to vesicles,whereas the morPhology aPPeared bigger sPherical micelles and smaller sPhere of S2 coexist then bigger sPherical micelles and lamellae coexist as the S2 rePlaced S1 . And the lengths of rod-like micelles and vesicles in diameter of S1/PS-b-PAA were statistic by i-TEM,which demonstrated that the sizes of rod-like micelles and vesicles lager at higher S1contents(from 251 nm→418 nm→1 280 nm). The aver-age Particle sizes of S2/PS-b-PAA measured by dynamic light scattering technology,the Particle size of micelles increased with the concentrations of S2 increased( from 134 nm→188 nm→1 597 nm). This re-sulted from the difference between the interactions of their alkyl chains with PS-b-PAA and the difference between the amounts of their ionic charge.