Synthesis and property characterization of acid dyeable acrylonitrile copolymer

Qinzhuo Zhou,Zhigang Shen,Hongyuan Zong,Qun Chen,Yingcheng Li

DOI: https://doi.org/10.3969/j.issn.1001-0041.2018.03.001

2018-01-01

Abstract:Acid-dye dyeable acrylonitrile copolymers with different molecular composition were prepared by using dimethylami -no ethyl methacrylate (DEMA) or methacryloyloxyethyl trimethyl ammonium chloride (DMC) as the third monomer via batch precipitation polymerization in aqueous phase .The structure and properties of the obtained copolymers were characterized by hy-drogen nuclear magnetic resonance spectroscopy , gel permeation chromatography , differential scanning calorimetry , dye up-take test and so on .The results showed that the polymerization process using one-pot initiator feeding method showed the characteristic of "dead-end polymerization", which led to the multimodal molecular weight distribution;the obtained copolymer had the viscosi-ty-average relative molecular mass of 50000-60000, the polydisperity index of 5-10, the monomodal molecular weight distribu-tion and conversion rate up to 70％ or so when the polymerization was initiated by semicontinuous process; the glass transition temperature was 101.2℃when the mass fraction of acrylonitrile was 90.3％in the copolymer;the dyeing property of the copoly-mer was related to the third monomer content and the molecular structure; the dye up-take was strongly dependent on the acid number of the dye bath when DEMA was used as the third monomer;the dyeing property of the copolymer was not sensitive to the pH value of the dye bath and remained fairly good with the dye up-take above 95％even in weak acid dyeing bath ( pH value of 5.0) when DMC was used as the third monomer .