Influences of Crosslinking Methods on Microstructure and Mechanical Properties of Soybean Protein Composite Films

Yunjiao Shi,Huajiang Zhang,Xuepeng Lü,Chunli Wei,Ang Li

DOI: https://doi.org/10.16429/j.1009-7848.2017.11.018

2017-01-01

Abstract:Soybean protein composite films were prepared using soy protein and gelatin as the main material,this work studies influence of solution crosslinking or steam crosslinking with glutaraldehyde on microstructure and mechanical properties of the composite films,with mechanical properties and microstructure as the evaluation.The results showed that when the glutaraldehyde was at a concentration of 0.20％ by solution crosslinking,the tensile strength of the composite films was maximum (3 120.26 ± 38.92) MPa,and elongation was (48.26 ± 1.92)％.While the maximum tensile strength of the steam crosslinking composite films was at a glutaraldehyde concentration of 0.15％.The tensile strength was (3 406.53± 32.47) MPa,and elongation was (39.53 ± 1.47)％.The stretching vibration of steam crosslinking significantly increased,its damage to the crystalline state was stronger than the solution crosslinking.The contact angle of steam crosslinking was 107.2°,significantly greater than the 84.7° of solution crosslinking,it reached a typical hydrophobic interface.In addition,the steam crosslinked composite films' surface and tensile fracture surface showed a dense smooth surface,forming a dense structure of three-dimensional network structure.Thus soybean protein composite films prepared by steam crosslinking were better than the composite films by solution crosslinking.