Dissolution behavior and solution properties of chitosan

Pei-yang NIU,Li-yan ZHANG

DOI: https://doi.org/10.13386/j.issn1002-0306.2017.06.007

2017-01-01

Abstract:The changes in transmittance,conductivity,viscosity and particle status of four kinds of chitosan solutions with different degree of deacetylation and molecular weight were mainly studied with different HCl and chitosan concentrations of 0～0.44 mol/L,6％ ～ 12％,respectively,under 50 ℃ and the dissolution trends and solution properties of chitosan were investigated.Results showed that when the HCl and chitosan concentration was 0.23～0.39 mol/L,6％ ～ 10％ respectively,the transmittance of chitosan solution increased dramatically,the higher the chitosan concentration and degree of acetylation,the higher the HCl concentration at which transmittance began to increase sharply.After finishing adding HCl,the lower the molecular weight of chitosan,the higher the final transmittance of chitosan solution.The conductivity of chitosan solution increased at a small and even ratio when HCl concentration was low.After HCl concentration was higher enough,the conductivity of solution rose at a ratio over 10 ms/cm,which indicated that chitosan was almost fully protonated.The higher the degree of deacetylation of chitosan,the higher the HCl concentration at which conductivity of solution increase dramatically.1#,2#,3#,4# chitosan solution reached the maximum viscosity at concentration of HCl of 0.29 mol/L,0.29 mol/L,0.34 mol/L,0.34 mol/L,respectively,then decreased significantly (p ＜ 0.05).Temperature increasing led to the decrease of solution viscosity,but the effect of temperature on viscosity was not changed.Microscopy observation showed that the number of chitosan particles decreased obviously with addition of hydrochloric acid.Chitosan with a higher degree of deacetylation fully disintegrated at a higher HCl concentration.The transmittance and conductivity of solution increased obviously at the stage at which of chitosan particles disintegrated fully.